Bayflex® XGT-80 (15% Glass)
| Category: | PUR-Ether/MDI , Polyurethane (Polyether, MDI) |
| Manufacturer: | Covestro - PUR |
| Trademark: | Bayflex® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | zmkr8v_Bayflex-XGT-80-15-Glass-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Bayflex XGT-80 is an elastomeric polyurethane system used in the reaction injection molding (RIM) process. The system is supplied as two liquid components: Component A is a modified diphenylmethane diisocyanate (MDI), and Component B is a polyether polyol system. Note: The polyol component phase-separates upon standing and must be thoroughly mixed via mechanical means prior to use. The extended gel time of Bayflex XGT-80 gives equipment designers the flexibility to create large, complex parts that can be molded on existing injection machinery. The resin's excellent surface quality and high impact resistance make it a candidate for agricultural equipment, heavy-duty trucks, specialty transportation, and marine applications. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.15 | g/cm³ | ASTM D792, ASTM D1622 |
| Molding Shrinkage - Flow (3.18 mm) | 0.55 - 0.65 | % | Internal method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, 3.18 mm) | 70 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break, 3.18 mm) | 26.2 | MPa | ASTM D638 |
| Tensile Elongation (Break, 3.18 mm) | 75 | % | ASTM D638 |
| Flexural Modulus | ASTM D790 | ||
| -30°C, 3.18 mm | 1930 | MPa | ASTM D790 |
| 23°C, 3.18 mm | 1170 | MPa | ASTM D790 |
| 70°C, 3.18 mm | 538 | MPa | ASTM D790 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tear Strength 1(3.18 mm) | 114 | kN/m | ASTM D624 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.18 mm) | 270 | J/m | ASTM D256 |
| Instrumented Dart Impact 2 | ASTM D3763 | ||
| -30°C, 3.18 mm | 2.71 | J | ASTM D3763 |
| 23°C, 3.18 mm | 7.73 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| CLTE - Flow (3.18 mm) | 5.6E-5 | cm/cm/°C | ASTM D696 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components 3 | |||
| Component a | Mixing ratio by weight: 140, mixing ratio by capacity: 120 | ||
| Component B | Mixing ratio by weight: 100, mixing ratio by capacity: 100 | ||
| Shelf Life 4(32°C) | 26 | wk | |
| Demold Time | 1.5 | min |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Sag - 4 in Overhang 5(121°C, 3.18 mm) | 9.91 | mm | ASTM D3769 |
| Part A Type: Isocyanate Appearance: Colorless to straw yellow liquid Specific Gravity @ 25°C: 1.21 Viscosity @25°C: 700 mPa-s Flash Point PMCC: 213 °C NCO: 22.6 - 23.1 % Part B Type: Polyol Appearance: Pale green to amber liquid Specific Gravity @ 25°C: 1.04 Viscosity @25°C: 550 mPa-s Flash Point PMCC: 112 °C Water: <0.09 wt% Molding Parameters Material Temperature - Component A: 32 to 38 °C Material Temperature - Component B: 43 to 49 °C Mold Temperature: 66 to 71 °C Polyol Nucleation - Specific Gravity: 0.9 0 shot time: 10 sec |
| Note Message | |
|---|---|
| 1 . | C mould |
| 2 . | 2.24 m/sec |
| 3 . | 1.05 Index |
| 4 . | 0.125 in |
| 5 . | 1 hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PTS PCA-1010HF | Polymer Technology and Services, LLC | PC+ABS | PTS |
| RETARDEL™ LSF-15 | HELLENIC CABLES S.A. | Polyolefin, Unspecified | RETARDEL™ |
| Desmovit® DP R Eco NF15 | geba Kunststoffcompounds GmbH | TPU-Ester/Ether | Desmovit® |
| DJSilicone NE-8171 | DONGJUE SILICONE (NANJING) CO., LTD | Silicone | DJSilicone |
| INEOS PP 100-GA01 | INEOS Olefins & Polymers Europe | PP Homopolymer | INEOS PP |