InnoGreen® BIO-80D
| Category: | TSU , Polyurethane Thermoset Elastomer |
| Manufacturer: | Innovative Polymers, Inc. |
| Trademark: | InnoGreen® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | zmVfAE_InnoGreen-BIO-80D.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| InnoGreen® BIO-80D is a 80 shore D polyurethane elastomer formulated for hand-batch and vacuum assisted processing. Excellent physical properties can be obtained with a room temperature cure without the utilization of mercury, MOCA or TDI InnoGreen® BIO-80D has been approved by the USDA as a bio preferred product. |
| General Information | |
|---|---|
| Features |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| Hardener | 1.03 | g/cm³ | |
| Cured | 1.14 | g/cm³ | |
| Base Resin | 1.20 | g/cm³ | |
| Molding Shrinkage - Flow | 0.20 to 0.50 | % | ASTM D2566 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus | 1380 | MPa | ASTM D790 |
| Flexural Strength | 55.2 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 48 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 65.0 | °C | ASTM D648 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Hardener | Mix Ratio by Volume: 100 Mix Ratio by Weight: 100 | ||
| Resin | Mix Ratio by Weight: 80 Mix Ratio by Volume: 86 | ||
| Demold Time | 120 to 240 | min |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Biobased Content | 39 | % |
| Uncured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Viscosity | |||
| 25°C 1 | 0.075 | Pa·s | |
| 25°C 2 | 0.53 | Pa·s | |
| 25°C 3 | 2.8 | Pa·s | |
| Curing Time 4 | 26 | hr | |
| Gel Time | 5.0 to 9.0 | min |
| Cured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 75 to 85 | ASTM D2240 | |
| Tensile Strength | 32.1 | MPa | ASTM D638 |
| Tensile Elongation at Break | 30 | % | ASTM D638 |
| Note Message | |
|---|---|
| 1 . | Resin |
| 2 . | Mixed |
| 3 . | Hardener |
| 4 . | 24 hours at 77°F + 2 hours at 150°F |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Veradel® 3100P | Solvay Specialty Polymers | PESU | Veradel® |
| AQUAFORCE® PA66 G30-01 SCHWARZ | LEIS Polytechnik - polymere Werkstoffe GmbH | Nylon 66 | AQUAFORCE® |
| Cheng Yu FV30G30 | Cheng Yu Plastic Company Limited | Acetal (POM) Homopolymer | Cheng Yu |
| Osterlene® PPH20NA | Osterman & Company | PP Homopolymer | Osterlene® |
| Sylvin 8952-65UV Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |