LNP™ LUBRICOMP™ DFL38 compound
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | zmKuOV_LNP-LUBRICOMP-DFL38-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP* LUBRICOMP* DFL38 is a compound based on Polycarbonate resin containing 40% Glass Fiber, 15% PTFE. Added feature of this material is: Wear Resistant. Also known as: LNP* LUBRICOMP* Compound DFL-4038 Product reorder name: DFL38 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | ASTM D792 | ||
| -- | 1.70 | g/cm³ | |
| -- | 1.69 | g/cm³ | |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.10 to 0.30 | % | |
| Across Flow : 24 hr | 0.30 to 0.50 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.060 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.090 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 11800 | MPa | ASTM D638 |
| -- | 12900 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 103 | MPa | ASTM D638 |
| Yield | 127 | MPa | ISO 527-2/5 |
| Break 3 | 103 | MPa | ASTM D638 |
| Break | 127 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 4 | 1.9 | % | ASTM D638 |
| Yield | 1.9 | % | ISO 527-2/5 |
| Break 5 | 1.9 | % | ASTM D638 |
| Break | 1.9 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 6 | 12100 | MPa | ASTM D790 |
| -- 7 | 11600 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 192 | MPa | ISO 178 |
| Yield, 50.0 mm Span 8 | 196 | MPa | ASTM D790 |
| Break, 50.0 mm Span 9 | 196 | MPa | ASTM D790 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| vs. Itself - Dynamic | 0.49 | ||
| vs. Itself - Static | 0.51 | ||
| Wear Factor - Washer | 23.5 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 140 | J/m | ASTM D256 |
| 23°C 10 | 13 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 650 | J/m | ASTM D4812 |
| 23°C 11 | 42 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact (23°C, Total Energy) | 17.3 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 143 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 12 | 145 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 137 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 13 | 138 | °C | ISO 75-2/Af |
| CLTE | ASTM D696 | ||
| Flow : -30 to 30°C | 2.9E-5 | cm/cm/°C | |
| Transverse : -30 to 30°C | 3.9E-5 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 293 to 304 | °C | |
| Middle Temperature | 310 to 321 | °C | |
| Front Temperature | 321 to 332 | °C | |
| Processing (Melt) Temp | 304 to 327 | °C | |
| Mold Temperature | 82.2 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | Type I, 5.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 1.3 mm/min |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 |
| 12 . | 80*10*4 mm |
| 13 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP EMI 1062 | RTP Company | PBT | RTP |
| NEFTEKHIM PP 2641J (T31SE) | Nizhnekamskneftekhim Inc. | PP Homopolymer | NEFTEKHIM PP |
| CARBEM® GFR 30 | EMAS Plastik San.Tic.AS. | PC | CARBEM® |
| Cheng Yu FV3035 | Cheng Yu Plastic Company Limited | Acetal (POM) Homopolymer | Cheng Yu |
| COPEC® CC8OCN (Series: VS/AD1) | KRAIBURG TPE | TPE | COPEC® |