MAJORIS DG300
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | AD majoris |
| Trademark: | MAJORIS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | zmGDVW_MAJORIS-DG300.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
MAJORIS DG300 is a polypropylene reinforced with glass fibres intended for injection moulding for outstanding properties for food contact regulations. This quality is also achieving low taste and odour high performances. MAJORIS DG300 has high rigidity and impact strength, good dimensional stability and good creep resistancy also at high temperatures. This quality is compatible with microwaves. MAJORIS DG300 is available in natural and other colours can be provided on request. MAJORIS DG300 fulfils RoHS compliance and is Yellow card listed. APPLICATIONS It can be used on applications requiring outstanding performances such as:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.12 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 6.0 | g/10 min | ISO 1133 |
| Molding Shrinkage (2.00 mm) | 0.60 - 0.80 | % | Internal method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness (H 358/30) | 120 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 6000 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 85.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Yield) | 2.2 | % | ISO 527-2/50 |
| Flexural Modulus 1 | ISO 178 | ||
| -- | 5600 | MPa | ISO 178 |
| 115°C | 3850 | MPa | ISO 178 |
| Flexural Stress 2 | ISO 178 | ||
| -- | 145 | MPa | ISO 178 |
| 115°C | 110 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -20°C | 9.0 | kJ/m² | ISO 179/1eA |
| 23°C | 12 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 53 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 150 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 145 | °C | ISO 75-2/A |
| Continuous Use Temperature | 120 | °C | |
| Vicat Softening Temperature | 164 | °C | ISO 306/A |
| CLTE - Flow | 3.0E-5 | cm/cm/°C | ISO 11359-2 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 | |
| Glow Wire Flammability Index (2.00 mm) | 750 | °C | IEC 60695-2-12 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 230 - 270 | °C | |
| Mold Temperature | 30.0 - 50.0 | °C | |
| Injection Rate | Moderate |
| Injection instructions |
|---|
| Holding pressure: 50 to 70% of the injection pressure |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Prime Tuff-X 200 HG | Primex Plastics Corporation | Unspecified | Prime Tuff-X |
| Vyncolit® RX®1-501AN (Nylon) | Vyncolit N.V. | DAP | Vyncolit® |
| XANTAR® 27 R | Mitsubishi Engineering-Plastics Corp | PC | XANTAR® |
| LUVOCOM® 1100-7725 VP | Lehmann & Voss & Co. | PESU | LUVOCOM® |
| omay® SE42W | Suzhou OMAY Optical Materials Co., Ltd | Film, PC | omay® |