LNP™ THERMOCOMP™ DF003E compound
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | zlhEZX_LNPTHERMOCOMPDF003Ecompound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP DF003E is a compound based on Polycarbonate resin containing Glass Fiber. Added features of this material include: Easy Molding. Also known as: LNP* THERMOCOMP* Compound DF-1003 EM Product reorder name: DF003E |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.31 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hours | 0.40 - 0.60 | % | ASTM D955 |
| Transverse flow : 24 hours | 0.50 - 0.70 | % | ASTM D955 |
| Vertical flow direction : 24 hours | 0.63 | % | ISO 294-4 |
| Flow direction : 24 hours | 0.54 | % | ISO 294-4 |
| Water Absorption (24 hr, 50% RH) | 0.10 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 4830 | MPa | ASTM D638 |
| -- | 4750 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield | 82.7 | MPa | ASTM D638 |
| Yield | 82.0 | MPa | ISO 527-2 |
| Fracture | 77.2 | MPa | ASTM D638 |
| Fracture | 78.0 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield | 3.2 | % | ASTM D638 |
| Yield | 3.3 | % | ISO 527-2 |
| Fracture | 5.0 | % | ASTM D638 |
| Fracture | 4.4 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 4140 | MPa | ASTM D790 |
| -- | 4300 | MPa | ISO 178 |
| Flexural Stress | 130 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 80 | J/m | ASTM D256 |
| 23°C 2 | 7.4 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 910 | J/m | ASTM D4812 |
| 23°C 3 | 56 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 20.4 | J | ASTM D3763 |
| -- | 6.70 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 3.20mm | 144 | °C | ASTM D648 |
| 0.45 MPa, unannealed, 64.0mm span 4 | 144 | °C | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 3.20mm | 139 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 5 | 139 | °C | ISO 75-2/Af |
| Linear thermal expansion coefficient | |||
| Flow : -40 to 40°C | 6.8E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Lateral : -40 to 40°C | 3.4E-5 | cm/cm/°C | ASTM E831 |
| Lateral : -40 to 40°C | 3.5E-5 | cm/cm/°C | ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 293 - 304 | °C | |
| Middle Temperature | 310 - 321 | °C | |
| Front Temperature | 321 - 332 | °C | |
| Processing (Melt) Temp | 304 - 327 | °C | |
| Mold Temperature | 82.2 - 110 | °C | |
| Back Pressure | 0.172 - 0.344 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| 5 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 2201 HF TFE 15 | RTP Company | PEEK | RTP |
| Unichem 5543 | Colorite Polymers | PVC, Flexible | Unichem |
| Elastron® G G500.A70.N.ABS | Elastron USA, Inc. | SEBS | Elastron® G |
| Hifax CA 7271 A | LyondellBasell Industries | TPO (POE) | Hifax |
| HONES® PBT GF30E | Guangdong Shunde Hones Polymer Material Co., Ltd. | PBT | HONES® |