| PC/ABS blend 10% glass fibre filled grade |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.20 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (260°C/5.0 kg) | 12 | g/10 min | ISO 1133 |
| Molding Shrinkage | 0.20 to 0.50 | % | ISO 2577 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2 | ||
| Yield | 60.0 | MPa | |
| Break | 58.0 | MPa | |
| Tensile Strain (Break) | 6.0 | % | ISO 527-2 |
| Flexural Modulus | 3900 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | ISO 180/1A | ||
| -30°C | 8.0 | kJ/m² | |
| 23°C | 12 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Annealed) | 115 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 138 | °C | ISO 306/A50 |
| -- | 130 | °C | ISO 306/B50 |
| Ball Pressure Test (75°C) | Pass |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+14 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+14 | ohms·cm | IEC 60093 |
| Electric Strength (1.00 mm, in Oil) | 33 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index | 250 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate | 35 | mm/min | FMVSS 302 |
| Flame Rating 1 | Internal Method | ||
| 1.60 mm | HB | ||
| 3.20 mm | HB | ||
| Glow Wire Flammability Index (2.00 mm) | 650 | °C | IEC 60695-2-12 |
| Note Message | |
|---|---|
| 1 . | UL94 internally tested |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 1701 TFE 5 | RTP Company | PPE | RTP |
| RTP 687 HEC | RTP Company | ABS | RTP |
| RTP 102 GB 25 | RTP Company | PP Homopolymer | RTP |
| AKROMID® A3 GK 30 1 natural (3673) | AKRO-PLASTIC GmbH | Nylon 66 | AKROMID® |
| Polybutene-1 DP8911ME | LyondellBasell Industries | PB | Polybutene-1 |