ALCUDIA® HDPE 5605-N
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | REPSOL |
| Trademark: | ALCUDIA® HDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | zl4sdg_ALCUDIAHDPE5605N.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| ALCUDIA® 5605-N is a bimodal high density polyethylene black compound with a special molecular structure to provide very low shrinkage during processing. Due to this outstanding characteristic, this grade is a very good product for optical fiber and contains a combination of antioxidant system with well dispersed carbon black which provide the following features: excellent protection against thermal oxidation during processing; long term stability and excellent outdoor weather resistance. This grade is widely used for sheathing of jelly-filled constructions and optical fiber. It is also suitable for power cable jacketing. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 0.958 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.45 | g/10 min | ISO 1133 |
| Environmental Stress-Cracking Resistance (F0) | > 1000 | hr | ASTM D1693 |
| Carbon Black Content | 2.3 | % | ASTM D1603 |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Retention of Mechanical Properties | ISO 527 | ||
| 10 days : 100°C | > 75 | % | ISO 527 |
| 14 days : 110°C | > 75 | % | ISO 527 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxygen sensing time (200°C) | > 30 | min | EN 728 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 64 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Break) | > 30.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | > 600 | % | ISO 527-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature 1 | -76.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 125 | °C | ISO 306/A |
| Electrical | Nominal Value | Test Method | |
|---|---|---|---|
| Dielectric Constant (1 MHz) | 2.50 | ASTM D1531 | |
| Dissipation Factor (1 MHz) | 5.0E-3 | ASTM D150 |
| Note Message | |
|---|---|
| 1 . | 0 Failures |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| CP PRYME® Polystyrene PS100BT-8M CLEAR | Chase Plastics Services Inc. | PS (GPPS) | CP PRYME® Polystyrene |
| Lucofin® 1411-t2 | Lucobit AG | Polyolefin, Unspecified | Lucofin® |
| Paracril® B | INSA | NBR | Paracril® |
| Pearlbond™ 520 | Lubrizol Advanced Materials, Inc. | TPU-Capro | Pearlbond™ |
| PIVINEL™ VHR-1 | HELLENIC CABLES S.A. | PVC, Unspecified | PIVINEL™ |