Order Products : sales@su-jiao.com
RX® 853G
| Category: | Phenolic , Phenolic |
| Manufacturer: | Sumitomo Bakelite North America, Inc. |
| Trademark: | RX® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | zkGZEe_RX-853G.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| RX® 853G is a fiberglass reinforced phenolic novolac compound, featuring dimensional stability, moderate impact resistance, and good strength and modulus. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.78 | g/cm³ | ASTM D792 |
| Apparent Density | 0.55 | g/cm³ | ASTM D1895 |
| Molding Shrinkage - Flow (Compression Molded) | 0.10 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.080 | % | ASTM D570 |
| Water Absorption - 48 hrs | 0.25 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (E-Scale, Compression Molded) | 80 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break, Compression Molded) | 55.0 | MPa | ASTM D638 |
| Flexural Modulus (Compression Molded) | 15900 | MPa | ASTM D790 |
| Flexural Strength (Compression Molded) | 103 | MPa | ASTM D790 |
| Compressive Strength | 190 | MPa | ASTM D695 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (Compression Molded) | 55 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 1.8 MPa, Unannealed, Compression Molded | 180 | °C | |
| 1.8 MPa, Annealed, Compression Molded | > 282 | °C | |
| CLTE | ASTM E831 | ||
| Flow | 2.0E-5 | cm/cm/°C | |
| Transverse | 3.9E-5 | cm/cm/°C | |
| Thermal Conductivity | 0.79 | W/m/K | ASTM C518 |
| RTI Elec | 150 | °C | UL 746 |
| RTI Imp | 150 | °C | UL 746 |
| RTI Str | 150 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength 1 | ASTM D149 | ||
| -- 2 | 14 | kV/mm | |
| -- 3 | 12 | kV/mm | |
| Arc Resistance | 185 | sec | ASTM D495 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.20 mm) | V-1 | UL 94 |
| Note Message | |
|---|---|
| 1 . | Wet, 60 Hz |
| 2 . | Method A (Short-Time) |
| 3 . | Method B (Step-by-Step) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Retpol® PDR 7408/2 UV3 | PolyPacific Pty. Ltd. | PP, Unspecified | Retpol® |
| Stirol UPS-0801 (1s.) | JSC CONCERN STIROL | PS (HIPS) | Stirol |
| Anjacom® 250-GF15 | Almaak International GmbH | Nylon 6 | Anjacom® |
| Desmopan® DP 2586A | Covestro - PUR | TPU-Polyester | Desmopan® |
| Kepamid® 2320GF | Korea Engineering Plastics Co., Ltd | Nylon 66 | Kepamid® |