Dynacom 104-G30HF
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | Dynachem Co. Ltd. |
| Trademark: | Dynacom |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ziiqnz_Dynacom-104-G30HF.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Dynacom 104-G30HF is a Polybutylene Terephthalate (PBT) material. It is available in Asia Pacific. Primary attribute of Dynacom 104-G30HF: Flame Rated. |
| General Information | |
|---|---|
| UL File Number |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.54 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow 1 | 0.30 to 1.0 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.070 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 2 | 85.0 | MPa | ASTM D638 |
| Tensile Elongation 3(Break) | 4.0 | % | ASTM D638 |
| Flexural Modulus 4 | 9020 | MPa | ASTM D790 |
| Flexural Strength 5 | 127 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm) | 59 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 205 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | V-0 | UL 94 |
| Note Message | |
|---|---|
| 1 . | Thickness: Thickness: 2 to 3 mm |
| 2 . | 5.0 mm/min |
| 3 . | 5.0 mm/min |
| 4 . | 3.0 mm/min |
| 5 . | 3.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxxam™ NT-818.G002-8000 | PolyOne Corporation | PP, Unspecified | Maxxam™ |
| PRL PPX-FR4 | Polymer Resources Ltd. | PPE+PS | PRL |
| AKROTEK® PEEK GF 30 natural (5047) | AKRO-PLASTIC GmbH | PEEK | AKROTEK® |
| Electrafil® PC CF20 FR IM BK | Techmer Engineered Solutions | PC | Electrafil® |
| MAJORIS DFR218 | AD majoris | PP, Unspecified | MAJORIS |