IROGRAN® A 80 P 4699 L
| Category: | TPU-Polyether , Thermoplastic Polyurethane Elastomer (Polyether) |
| Manufacturer: | Huntsman Corporation |
| Trademark: | IROGRAN® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ziEQeQ_IROGRAN-A-80-P-4699-L.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
IROGRAN A 80 P 4699 L is a high performance polyether based thermoplastic polyurethane intended for extrusion and injection mold applications. IROGRAN A 80 P 4699 L is part of the HUNTSMAN extrusion / injection mold product range. PERFORMANCE FEATURES
|
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity 1 | 1.09 | g/cm³ | ASTM D792 |
| Melt Volume-Flow Rate (MVR) (190°C/21.6 kg) | 140 | cm³/10min | |
| Molding Shrinkage - Flow (Injection Molded) | 11 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A, Injection Molded) | 81 | ASTM D2240, DIN 53505 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Abrasion 2 | |||
| -- | 54 | mm³ | |
| -- | 50 | mm³ | DIN 53515 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress 3 | |||
| 100% Strain, 0.635 mm | 5.93 | MPa | ASTM D412 |
| 100% Strain, 0.635 mm | 5.70 | MPa | DIN 53504 |
| 300% Strain, 0.635 mm | 8.27 | MPa | ASTM D412 |
| 300% Strain, 0.635 mm | 8.40 | MPa | DIN 53504 |
| Tensile Strength 4 | |||
| Break, 0.635 mm | 21.0 | MPa | ASTM D412 |
| Break, 0.635 mm | 30.0 | MPa | DIN 53504 |
| Tensile Elongation 5 | |||
| Break, 0.635 mm | 810 | % | ASTM D412 |
| Break, 0.635 mm | 750 | % | DIN 53504 |
| Tear Strength 6 | |||
| 0.635 mm | 89.3 | kN/m | ASTM D624 |
| 0.635 mm | 45 | kN/m | DIN 53515 |
| Compression Set 7 | ASTM D395, DIN 53517 | ||
| 23°C, 22 hr | 24 | % | |
| 70°C, 22 hr | 46 | % |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature 8 | 126 to 150 | °C | TMA |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 85.0 to 90.0 | °C | |
| Drying Time | 4.0 | hr | |
| Hopper Temperature | 175 | °C | |
| Cylinder Zone 1 Temp. | 180 | °C | |
| Cylinder Zone 2 Temp. | 180 | °C | |
| Cylinder Zone 3 Temp. | 180 | °C | |
| Cylinder Zone 4 Temp. | 180 | °C | |
| Cylinder Zone 5 Temp. | 180 | °C | |
| Adapter Temperature | 180 | °C | |
| Die Temperature | 175 | °C |
| Note Message | |
|---|---|
| 1 . | Injection Molded |
| 2 . | Injection Molded |
| 3 . | Extruded Film |
| 4 . | Extruded Film |
| 5 . | Extruded Film |
| 6 . | Extruded Film |
| 7 . | Injection Molded |
| 8 . | Extruded Film, 0.025 in |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Vinnolit® EP 7555 | Vinnolit GmbH & Co. KG | PVC Homopolymer | Vinnolit® |
| Novalloy-A A2604 | PlastxWorld Inc. | ABS+Nylon | Novalloy-A |
| Boltaron 1050 | Boltaron Performance Products | PVC, Unspecified | Boltaron |
| CYCOLAC™ MG94U resin | SABIC Innovative Plastics | ABS | CYCOLAC™ |
| Sylvin 29168-70 Clear | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |