4LEX® 10F10400
| Category: | PC , Polycarbonate |
| Manufacturer: | 4Plas |
| Trademark: | 4LEX® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | zi9eK5_4LEX-10F10400.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 4LEX 10F10400 is a Low Flow UV Stabilised Polycarbonate |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.20 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/3.8 kg) | 6.0 | g/10 min | ISO 1133 |
| Molding Shrinkage - Across Flow | 0.50 | % | |
| Water Absorption 1(Equilibrium, 23°C, 50% RH) | 0.15 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 2350 | MPa | ISO 527-2/5 |
| Tensile Stress | ISO 527-2/5 | ||
| Yield, 23°C | 58.0 | MPa | ISO 527-2/5 |
| Fracture, 23°C | 52.0 | MPa | ISO 527-2/5 |
| Tensile Strain | |||
| Yield | 8.0 | % | ISO 527-2 |
| Fracture, 23°C | 93 | % | ISO 527-2/5 |
| Flexural Stress | 90.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 19 | kJ/m² | ISO 179/B |
| Notched Izod Impact | ISO 180/1A | ||
| -30°C | 15 | kJ/m² | ISO 180/1A |
| 23°C | 60 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 144 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 145 | °C | ISO 306/B |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index | 250 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.60 mm | HB | UL 94 | |
| 3.20 mm | HB | UL 94 | |
| Glow Wire Flammability Index (2.00 mm) | 870 | °C | IEC 60695-2-12 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Transmittance (3000 µm) | 80.0 - 90.0 | % | ASTM D1003 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Processing (Melt) Temp | 260 - 300 | °C | |
| Mold Temperature | 80.0 - 100 | °C | |
| Injection Rate | Moderate-Fast | ||
| Holding Pressure | 60.0 - 120 | MPa | |
| Screw Speed | 200 | rpm |
| Injection instructions |
|---|
| Feed Throat Temperature: 60 - 80 °CBack Pressure: Low |
| Note Message | |
|---|---|
| 1 . | 24 Hrs |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Rilsan® KMVO 39099 TL | Arkema | Nylon 11 | Rilsan® |
| Toraypef® 15020 AP5M | Toray Resin Company | Polyolefin, Unspecified | Toraypef® |
| Unichem 4060A | Colorite Polymers | PVC, Unspecified | Unichem |
| Utomer UT1CP85AC | Shanghai Utomer Material Science Co., Ltd. | TPU-Polyester | Utomer |
| HIPOLEN P® FB 4T | HIPOL A.D. | PP Homopolymer | HIPOLEN P® |