POLYLAN T-035
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | POLYMA Kunststoff GmbH & Co. KG |
| Trademark: | POLYLAN |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | zhmWQ0_POLYLAN-T-035.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| POLYLAN T-035 is an Acrylonitrile Butadiene Styrene (ABS) product. It is available in Europe. Primary characteristic: flame rated. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.04 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (200°C/10.0 kg) | 3.5 | g/10 min | ASTM D1238, ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale, 23°C) | 100 | ASTM D785, ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 2260 | MPa | ASTM D638, ISO 527-2 |
| Tensile Strength (Yield, 23°C) | 43.0 | MPa | ASTM D638, ISO 527-2 |
| Flexural Strength (23°C) | 69.0 | MPa | ASTM D790, ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 6.35 mm) | 340 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed, 12.7 mm | 91.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 91.0 | °C | ISO 75-2/A |
| 1.8 MPa, Annealed, 12.7 mm | 104 | °C | ASTM D648 |
| 1.8 MPa, Annealed | 104 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 107 | °C | ISO 306/A, ASTM D1525 1 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.59 mm) | HB | UL 94 |
| Note Message | |
|---|---|
| 1 . | Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® N8960 | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| THERMOLAST® K TC5FRN (Series: FR) | KRAIBURG TPE | TPE | THERMOLAST® K |
| Baoding 68T85 | Baoding Bangtai Polymeric New-Materials Co.,Ltd | TPU-Polyester | Baoding |
| HIFOR Xtreme® SC74858 | Westlake Chemical Corporation | LLDPE | HIFOR Xtreme® |
| LEXAN™ 123 resin | SABIC Innovative Plastics | PC | LEXAN™ |