SNOLEN® EF 0.21/46 HT
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | JSC Gazprom neftekhim Salavat |
| Trademark: | SNOLEN® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | zh3sze_SNOLEN-EF-0-21-46-HT.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
CHARACTERISTIC PROPERTIES Good impact resistance by free-falling dart method (puncture resistance by falling weight test). Good tensile strength at break. MAJOR APPLICATIONS Ultrastrong packing. Bags. Bin bags. A multilayer film component. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 0.942 to 0.946 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 190°C/21.6 kg | 0.15 to 0.21 | g/10 min | |
| 190°C/5.0 kg | 3.6 to 7.2 | g/10 min | |
| Melt Flow Ratio | 26.0 to 34.0 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Elmendorf Tear Strength | |||
| MD | 509.9 | g/2.5 cm | |
| TD | 1019.7 | g/2.5 cm |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 58 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2/50 | ||
| Yield | 21.0 | MPa | |
| Break | 36.0 | MPa |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Recommended / Available | 10 to 200µm | ||
| Tensile Stress | ISO 527-3/50 | ||
| MD : Break | 45.0 | MPa | |
| TD : Break | 40.0 | MPa | |
| Tensile Elongation | ISO 527-3/50 | ||
| MD : Break | 450 | % | |
| TD : Break | 500 | % | |
| Dart Drop Impact | 240 | g | ASTM D1709 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -80.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 73.0 | °C | ISO 306/B50 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 200 to 230 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tecomid® NA40 GR25 NL XA60 | Eurotec Engineering Plastics | Nylon 66 | Tecomid® |
| Tenite™ Butyrate 285A2R30018 Natural, Trsp | Eastman Chemical Company | CAB | Tenite™ Butyrate |
| Alathon® L4907 | LyondellBasell Industries | HDPE, HMW | Alathon® |
| Hylon® N1240MHL | Ravago Manufacturing Americas, LLC | Nylon 66 | Hylon® |
| FUDOWLITE® F5636F | Fudow Co., Ltd. | Phenolic | FUDOWLITE® |