Generic PP Homopolymer
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | zgy9k2_Generic-PP-Homopolymer.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic PP Homopolymer This information is provided for comparative purposes only. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 0.890 - 0.912 | g/cm³ | ASTM D792 |
| 23°C | 0.853 - 0.947 | g/cm³ | ISO 1183 |
| -- | 0.900 - 0.908 | g/cm³ | ASTM D1505 |
| Apparent Density | 0.50 | g/cm³ | ASTM D1895 |
| Melt Mass-Flow Rate (MFR) | |||
| 230°C/2.16 kg | 0.30 - 45 | g/10 min | ASTM D1238 |
| 230°C/2.16 kg | 0.28 - 45 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (230°C/2.16 kg) | 1.10 - 63.6 | cm³/10min | ISO 1133 |
| Molding Shrinkage | |||
| Flow : 23°C | 0.99 - 2.0 | % | ASTM D955 |
| Transverse flow : 23°C | 1.2 - 2.3 | % | ASTM D955 |
| 23°C | 1.3 - 1.5 | % | ISO 294-4 |
| Water Absorption | ASTM D570 | ||
| 23°C, 24 hr | 0.010 - 0.031 | % | ASTM D570 |
| Saturated, 23°C | 0.010 - 0.020 | % | ASTM D570 |
| Equilibrium, 23°C | 0.010 - 0.011 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | |||
| 23°C | 87 - 111 | ASTM D785 | |
| 23°C | 90 - 111 | ISO 2039-2 | |
| Durometer Hardness | |||
| 23°C | 67 - 98 | ASTM D2240 | |
| 23°C | 70 - 75 | ISO 868 | |
| Ball Indentation Hardness | 65.8 - 80.8 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| 23°C | 1230 - 1870 | MPa | ASTM D638 |
| 23°C | 1250 - 2000 | MPa | ISO 527-2 |
| Tensile Strength | |||
| Yield, 23°C | 31.0 - 39.0 | MPa | ASTM D638 |
| Yield, 23°C | 29.9 - 38.4 | MPa | ISO 527-2 |
| Fracture, 23°C | 18.4 - 44.3 | MPa | ASTM D638 |
| Fracture, 23°C | 18.8 - 35.0 | MPa | ISO 527-2 |
| 23°C | 20.0 - 37.4 | MPa | ASTM D638 |
| 23°C | 22.0 - 31.3 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield, 23°C | 1.0 - 21 | % | ASTM D638 |
| Yield, 23°C | 7.4 - 11 | % | ISO 527-2 |
| Fracture, 23°C | 4.0 - 500 | % | ASTM D638 |
| Fracture, 23°C | 36 - 110 | % | ISO 527-2 |
| Flexural Modulus | |||
| 23°C | 973 - 1720 | MPa | ASTM D790 |
| 23°C | 1140 - 1710 | MPa | ISO 178 |
| Flexural Strength | |||
| 23°C | 25.0 - 47.2 | MPa | ASTM D790 |
| 23°C | 17.0 - 50.3 | MPa | ISO 178 |
| Yield, 23°C | 32.7 - 51.7 | MPa | ASTM D790 |
| Coefficient of Friction | 0.17 - 1.0 | ASTM D1894 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 20 - 94 | µm | |
| secant modulus | |||
| MD | 621 - 2760 | MPa | ASTM D882 |
| TD | 490 - 4830 | MPa | ASTM D882 |
| 23°C | 430 - 801 | MPa | ISO 527-3 |
| Tensile Stress | |||
| Yield, 23°C | 21.8 - 28.2 | MPa | ISO 527-3 |
| MD : Fracture | 27.5 - 250 | MPa | ASTM D882 |
| TD : Fracture | 25.5 - 263 | MPa | ASTM D882 |
| Fracture, 23°C | 33.8 - 45.4 | MPa | ISO 527-3 |
| 23°C | 35.0 - 46.0 | MPa | ISO 527-3 |
| Tensile Elongation | |||
| MD : Fracture | 78 - 860 | % | ASTM D882 |
| TD : Fracture | 15 - 800 | % | ASTM D882 |
| Fracture, 23°C | 500 - 710 | % | ISO 527-3 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 1.0 - 6.1 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 2.0 - 190 | kJ/m² | ISO 179 |
| Notched Izod Impact | |||
| 23°C | 19 - 51 | J/m | ASTM D256 |
| 23°C | 1.6 - 6.5 | kJ/m² | ISO 180 |
| Unnotched Izod Impact | |||
| 23°C | 22 - 1100 | J/m | ASTM D256 |
| 23°C | 20 - 60 | kJ/m² | ISO 180 |
| Dart Drop Impact (23°C) | 0.00 - 6.21 | J | ASTM D5420 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, not annealed | 85.7 - 125 | °C | ASTM D648 |
| 0.45 MPa, not annealed | 78.0 - 106 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 48.5 - 110 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 50.2 - 60.4 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 149 - 156 | °C | ASTM D1525 |
| -- | 88.5 - 157 | °C | ISO 306 |
| Melting Temperature | |||
| -- | 159 - 166 | °C | |
| -- | 165 - 166 | °C | DSC |
| -- | 160 - 165 | °C | ISO 11357-3 |
| -- | 162 - 165 | °C | ASTM D3418 |
| -- | 163 - 165 | °C | ISO 3146 |
| Peak Crystallization Temperature (DSC) | 109 - 164 | °C | ASTM D3418 |
| CLTE - Flow | 6.5E-5 - 1.6E-4 | cm/cm/°C | ASTM D696 |
| RTI Elec | 65.0 - 115 | °C | UL 746 |
| RTI Imp | 65.0 - 115 | °C | UL 746 |
| RTI | 65.0 - 115 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | |||
| -- | 50 - 1.0E+15 | ohms | ASTM D257 |
| -- | 1.0E+11 - 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | |||
| 23°C | 7.5E+15 - 1.0E+17 | ohms·cm | ASTM D257 |
| 23°C | 1.0E+13 - 1.0E+15 | ohms·cm | IEC 60093 |
| Dielectric Strength (23°C) | 20 - 43 | kV/mm | ASTM D149 |
| Comparative Tracking Index | 594 - 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate | 0.0 - 100 | mm/min | ISO 3795 |
| Glow Wire Flammability Index | 850 - 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature | 743 - 960 | °C | IEC 60695-2-13 |
| Oxygen Index | 25 - 26 | % | ASTM D2863 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss | 50 - 157 | ASTM D2457 | |
| Haze | 0.10 - 3.6 | % | ASTM D1003 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 69.9 - 105 | °C | |
| Drying Time | 2.0 - 3.0 | hr | |
| Suggested Max Regrind | 20 | % | |
| Hopper Temperature | 50.0 - 60.0 | °C | |
| Rear Temperature | 179 - 223 | °C | |
| Middle Temperature | 192 - 251 | °C | |
| Front Temperature | 194 - 260 | °C | |
| Nozzle Temperature | 188 - 250 | °C | |
| Processing (Melt) Temp | 187 - 251 | °C | |
| Mold Temperature | 30.0 - 65.4 | °C | |
| Injection Pressure | 6.55 - 103 | MPa | |
| Holding Pressure | 35.0 - 36.1 | MPa | |
| Back Pressure | 0.241 - 7.50 | MPa |
| Injection instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic PP HomopolymerThis information is provided for comparative purposes only. |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 175 - 252 | °C | |
| Cylinder Zone 2 Temp. | 175 - 262 | °C | |
| Cylinder Zone 3 Temp. | 175 - 262 | °C | |
| Cylinder Zone 4 Temp. | 175 - 277 | °C | |
| Cylinder Zone 5 Temp. | 175 - 277 | °C | |
| Melt Temperature | 214 - 251 | °C | |
| Die Temperature | 200 - 250 | °C |
| Extrusion instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic PP HomopolymerThis information is provided for comparative purposes only. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Teldene® H03ML | National Petrochemical Industries Company (NATPET) | PP Homopolymer | Teldene® |
| NITRIFLEX NTL-218 | NITRIFLEX | SBR, Unspecified | NITRIFLEX |
| Hyrene® PS-HI 14/2 | Entec Polymers | PS (HIPS) | Hyrene® |
| Karina IVORY PVC COMPOUND -E 832-35/ 1-Y-ERA-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Durethan® AKV 35 000000 | LANXESS GmbH | Nylon 66 | Durethan® |