ASTAMID™ MA3K
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Marplex Australia Pty. Ltd. |
| Trademark: | ASTAMID™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | zgm56V_ASTAMID-MA3K.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| ASTAMID™ MA3K is a heat stabilised, easy flow Polyamide 66 grade designed for fast processing. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.13 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.20 mm) | 1.0 | % | ASTM D955 |
| Water Absorption | |||
| 24 hr | 0.90 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 2.8 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1(3.20 mm) | 3150 | MPa | ASTM D638 |
| Tensile Strength 2(3.20 mm) | 85.0 | MPa | ASTM D638 |
| Tensile Elongation 3(Break, 3.20 mm) | 5.0 | % | ASTM D638 |
| Flexural Modulus 4(3.20 mm) | 3100 | MPa | ASTM D790 |
| Flexural Strength 5(3.20 mm) | 115 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | 55 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm) | 77.0 | °C | ASTM D648 |
| CLTE - Flow | 7.0E-4 | cm/cm/°C | ASTM D696 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 75.0 - 85.0 | °C | |
| Drying Time | 2.0 | hr | |
| Rear Temperature | 275 - 285 | °C | |
| Middle Temperature | 285 - 295 | °C | |
| Front Temperature | 285 - 295 | °C | |
| Processing (Melt) Temp | 270 - 290 | °C | |
| Mold Temperature | 50.0 - 80.0 | °C | |
| Injection Pressure | 60.0 - 130 | MPa | |
| Injection Rate | Moderate | ||
| Back Pressure | 0.100 - 0.500 | MPa | |
| Screw Speed | 40 - 60 | rpm | |
| Clamp Tonnage | 3.0 - 5.0 | kN/cm² |
| Injection instructions |
|---|
| Drying Time (Opened Bag): >12 hr |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| VYLOPET® EMC341 | TOYOBO America, Inc. | PC+PBT | VYLOPET® |
| Bayblend® M750 | Covestro - Polycarbonates | PC+ABS | Bayblend® |
| Bergamid™ A700 G30 H | PolyOne Corporation | Nylon 66 | Bergamid™ |
| Dynalloy™ GP 7830-60N | PolyOne Corporation | TPE | Dynalloy™ |
| VALOX™ 855 resin | SABIC Innovative Plastics | PBT | VALOX™ |