Hostacom M2 N01 L304698
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Hostacom |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | zgkNM0_Hostacom-M2-N01-L304698.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| "Hostacom" M2 N01 L304698 is a 20% mineral filled polypropylene homopolymer The product is designed for injection molding of dishwasher parts and is available in a not color matched light grey color. UL listing only in grey. It is not intended for medical or pharmaceutical applications. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.05 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/5.0 kg) | 9.0 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (230°C/5.0 kg) | 10.0 | cm³/10min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness (H 358/30) | 85.0 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus - Secant (23°C) | 2800 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 36.0 | MPa | ISO 527-2/50 |
| Tensile Strain | ISO 527-2/50 | ||
| Yield | 5.0 | % | |
| Break | > 15 | % | |
| Flexural Modulus - Secant | 2900 | MPa | ISO 178 |
| Flexural Stress (3.5% Strain) | 45.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -20°C | 2.0 | kJ/m² | |
| 23°C | 4.5 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -20°C | 25 | kJ/m² | |
| 23°C | 50 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 115 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 65.0 | °C | ISO 75-2/A |
| RTI Elec | 65.0 | °C | UL 746 |
| RTI Imp | 65.0 | °C | UL 746 |
| RTI Str | 65.0 | °C | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| tivilon® M 65 DX 4 | API SpA | TPV | tivilon® |
| NuSil CV-8151 | NuSil Technology | Silicone | NuSil |
| Elastamax™ HTE 3080 | PolyOne Corporation | PVC+NBR | Elastamax™ |
| HIPOLEN P® MA 31 | HIPOL A.D. | PP Homopolymer | HIPOLEN P® |
| LNP™ THERMOCOMP™ LC003E compound | SABIC Innovative Plastics | PEEK | LNP™ THERMOCOMP™ |