ALTECH® PP-B B 4430/500 MR30
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | ALBIS PLASTIC GmbH |
| Trademark: | ALTECH® PP-B |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | zgk7fC_ALTECHPPBB4430500MR30.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ALTECH®PP-B B 4430/500 MR30 is a polypropylene copolymer (PP Copoly) product, which contains 30% mineral fillers. It can be processed by injection molding and is available in North America, Europe or the Asia-Pacific region. ALTECH®The application fields of PP-B B 4430/500 MR30 include construction application, housing, engineering/industrial accessories and automobile industry. Features include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.09 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 9.0 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (230°C/2.16 kg) | 9.00 | cm³/10min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1300 | MPa | ISO 527-2 |
| Tensile Stress | 15.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 90 | % | ISO 527-2 |
| Flexural Modulus | 1400 | MPa | ISO 178 |
| Flexural Stress | 25.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -- | 16 | kJ/m² | ISO 179/1eA |
| -40°C | 3.0 | kJ/m² | ISO 179/1eA |
| -20°C | 3.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -- | No Break | ISO 179/1eU | |
| -40°C | 20 | kJ/m² | ISO 179/1eU |
| -20°C | 26 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 55.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 60.0 | °C | ISO 306/B50 |
| -- | 64.0 | °C | ISO 306/B120 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| Dehumidification desiccant | 60 - 90 | °C | |
| Hot air dryer | 60 - 90 | °C | |
| Drying Time | |||
| Dehumidification desiccant | 2.0 - 4.0 | hr | |
| Hot air dryer | 2.0 - 4.0 | hr | |
| Processing (Melt) Temp | 200 - 270 | °C | |
| Mold Temperature | 20 - 70 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Microthene® F FA70900 | LyondellBasell Industries | HDPE | Microthene® F |
| INELEC PEICF10 | Infinity LTL Engineered Compounds | PEI | INELEC |
| IROSTIC® S 7514 | Huntsman Corporation | TPU, Unspecified | IROSTIC® |
| LinGen FR290 | Shanghai Lin Gen Rubber Materials Co., Ltd. | TPE | LinGen |
| MARPOL® FS3 | Marco Polo International, Inc. | PS (EPS) | MARPOL® |