Badamid® A70 GK30
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Bada AG |
| Trademark: | Badamid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | zgKbqP_Badamid-A70-GK30.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Injection moulding grade with 30% of glass beads with good mechanical properties and high dimensional stability |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.36 | -- | g/cm³ | ISO 1183 |
| Water Absorption | ISO 62 | |||
| Saturation, 23°C | 6.0 | -- | % | |
| Equilibrium, 23°C, 50% RH | 2.0 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus 1(23°C) | 4800 | 2650 | MPa | ISO 527-2/1 |
| Tensile Stress 2(Break, 23°C) | 95.0 | 70.0 | MPa | ISO 527-2/5 |
| Tensile Strain 3(Break, 23°C) | 6.0 | 9.0 | % | ISO 527-2/5 |
| Flexural Stress 4(23°C) | 185 | 135 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength 5 | ISO 179/1eA | |||
| -30°C | 5.0 | 6.0 | kJ/m² | |
| 23°C | 6.0 | 8.0 | kJ/m² | |
| Notched Izod Impact Strength 6 | ISO 180/1A | |||
| -30°C | 4.0 | 7.0 | kJ/m² | |
| 23°C | 5.0 | 8.0 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature 7 | ||||
| 0.45 MPa, Unannealed | 210 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 105 | -- | °C | ISO 75-2/A |
| Melting Temperature (DSC) 8 | 262 | -- | °C | ISO 3146 |
| Maximum Service Temperature | IEC 216 | |||
| 20000 hrs | 110 | -- | °C | |
| some hours | 220 | -- | °C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity 9 | 1.0E+12 | 1.0E+10 | ohms | IEC 60093 |
| Volume Resistivity 10 | 1.0E+15 | 1.0E+12 | ohms·cm | IEC 60093 |
| Relative Permittivity 11(1 MHz) | 3.50 | 5.50 | IEC 60250 | |
| Dissipation Factor 12(1 MHz) | 0.026 | 0.20 | IEC 60250 | |
| Comparative Tracking Index | 500 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 0.800 mm 13 | HB | -- | ||
| 1.60 mm 14 | HB | -- |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Processing (Melt) Temp | 280 to 305 | °C | |
| Mold Temperature | 80.0 to 100 | °C |
| Note Message | |
|---|---|
| 1 . | Test Specimen accordng to ISO 3167, Type A |
| 2 . | Test Specimen accordng to ISO 3167, Type A |
| 3 . | Test Specimen accordng to ISO 3167, Type A |
| 4 . | 80x10x4 mm |
| 5 . | 80x10x4 mm |
| 6 . | 80x10x4 mm |
| 7 . | 110x10x4mm |
| 8 . | 10 K/min, Compound for moulding |
| 9 . | 80x80x1 mm |
| 10 . | 80x80x1 mm |
| 11 . | 80x80x1 mm |
| 12 . | 80x80x1 mm |
| 13 . | 125x13x0.8 mm |
| 14 . | 125x13x1.6 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Monprene® PC-12153 | Teknor Apex Company | TPE | Monprene® |
| Vipel® F282-AAN-00 | AOC, L.L.C. | Polyester Alloy | Vipel® |
| TRIREX® Compound 3025N1 | Samyang Corporation | PC | TRIREX® Compound |
| DEXFLEX® D60-UV 4LLA | LyondellBasell Industries | TPO (POE) | DEXFLEX® |
| Sylvin 8368-70DUV Black | Sylvin Technologies Incorporated | PVC, Semi-Rigid | Sylvin |