SAXAMID™ 126F7
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | SAX Polymers |
| Trademark: | SAXAMID™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | zgCl17_SAXAMID-126F7.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| SAXAMID 126F7 is a polyamide 6 injection-molding-grade reinforced with 35 % glass fibres. Because of its high strength and stiffness this grade is often used for stressed parts. Additionally properties are very good processability and good surface quality. This product is UL listed. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.41 | g/cm³ | ISO 1183 |
| Viscosity Number (H2SO4 (Sulphuric Acid)) | 150 | cm³/g | ISO 307 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 10300 | MPa | ISO 527-2/1 |
| Tensile Stress | 193 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 4.0 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 8800 | MPa | ISO 178 |
| Flexural Stress 2 | 293 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 11 | kJ/m² | |
| 23°C | 13 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 80 | kJ/m² | |
| 23°C | 85 | kJ/m² | |
| Notched Izod Impact Strength | ISO 180/1A | ||
| -30°C | 10 | kJ/m² | |
| 23°C | 13 | kJ/m² | |
| Unnotched Izod Impact Strength | ISO 180/1U | ||
| -30°C | 79 | kJ/m² | |
| 23°C | 82 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 3(1.8 MPa, Unannealed, 60.0 mm Span) | 209 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 216 | °C | ISO 306/B120 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flammability Classification (1.50 to 1.70 mm) | HB | IEC 60695-11-10, -20 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 to 6.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Processing (Melt) Temp | 260 to 290 | °C | |
| Mold Temperature | 70.0 to 90.0 | °C |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 80*10*4mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TORZEN Marathon™ FRU4800XHL BK01 | INVISTA Engineering Polymers | Nylon 66 | TORZEN Marathon™ |
| Akulon® K222-DL | DSM Engineering Plastics | Nylon 6 | Akulon® |
| HiFill® PA6 GF20 L | Techmer Engineered Solutions | Nylon 6 | HiFill® |
| LNP™ THERMOCOMP™ WF008 compound | SABIC Innovative Plastics | PBT | LNP™ THERMOCOMP™ |
| POLYelast TPE EC90 D50 P05B | Polykemi AB | PP+EPDM | POLYelast |