Latilub 66-01M
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | LATI S.p.A. |
| Trademark: | Latilub |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | zg7lye_Latilub-66-01M.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Self-lubricating product based on Polyamide 66 (PA 66). Molybdenum dysulphide. Product UL certified. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.14 | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | ISO 294-4 | ||
| Across Flow : 2.00 mm | 1.3 to 1.6 | % | |
| Flow : 2.00 mm | 1.2 to 1.5 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 3700 | MPa | ISO 527-2/1 |
| Tensile Stress (Break, 23°C) | 85.0 | MPa | ISO 527-2/5 |
| Tensile Strain | ISO 527-2/5 | ||
| Yield, 23°C | 9.0 | % | |
| Break, 23°C | 11 | % | |
| Coefficient of Friction | ASTM D3702 | ||
| vs. Itself - Dynamic | 0.27 | ||
| vs. Itself - Static | 0.29 | ||
| Wear Factor | 7.00E-9 | (m³/h)/(N·m·h) | ASTM D3702 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 4.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | No Break | ISO 179/1eU | |
| Notched Izod Impact (23°C, 3.20 mm) | 35 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 235 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 90.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 240 | °C | ISO 306/B50 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (0.750 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 to 100 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 260 to 290 | °C | |
| Mold Temperature | 70.0 to 90.0 | °C | |
| Injection Rate | Moderate |
| Note Message | |
|---|---|
| 1 . | at 60 Mpa of cavity pressure |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Veroplas SKG10 | PlastxWorld Inc. | ABS | Veroplas |
| ABS Proquigel GSE | Proquigel | ABS | ABS Proquigel |
| DJSilicone NE-G160 | DONGJUE SILICONE (NANJING) CO., LTD | Silicone | DJSilicone |
| Dynacom TY-5B | Dynachem Co. Ltd. | PP Copolymer | Dynacom |
| LNP™ VERTON™ MV006S compound | SABIC Innovative Plastics | PP, Unspecified | LNP™ VERTON™ |