RTP 200D TFE 20 SI 2.5
| Category: | Nylon 612 , Polyamide 612 |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | zg5chc_RTP-200D-TFE-20-SI-2-5.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Warning: The status of this material is 'Commercial: Limited Issue' The data for this material has not been recently verified. Please contact RTP Company for current information prior to specifying this grade. -Preliminary Product Data per RTP Co.- |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.19 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 1.1 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.30 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 118 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1860 | MPa | ASTM D638 |
| Tensile Strength | 48.3 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 9.5 | % | ASTM D638 |
| Flexural Modulus | 1720 | MPa | ASTM D790 |
| Flexural Strength | 62.1 | MPa | ASTM D790 |
| Compressive Strength | 27.6 | MPa | ASTM D695 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (6.35 mm) | 53 | J/m | ASTM D256 |
| Unnotched Izod Impact (6.35 mm) | 430 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 204 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 93.3 | °C | ASTM D648 |
| CLTE - Flow | 9.0E-5 | cm/cm/°C | ASTM D696 |
| Thermal Conductivity | 0.23 | W/m/K | ASTM C177 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+13 | ohms·cm | ASTM D257 |
| Dielectric Strength | 20 | kV/mm | ASTM D149 |
| Dielectric Constant (1 MHz) | 3.60 | ASTM D150 | |
| Dissipation Factor (1 MHz) | 0.015 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.59 mm) | HB | UL 94 |
| Additional Information |
|---|
| Mold Shrinkage, Linear-Flow, ASTM D-955, 0.25in.: 15mil/in.Tensile Elongation, ASTM D-638: 9-10%Wear Factor, K, ASTM D-3702: 15E-10in³/min/ft/lb/hrCoefficient of Friction, ASTM 3702, Dynamic: 0.10The coefficient of friction and wear factor were tested on a Falex Model No.6 Wear Testing Machine at 50 FPM, 2000 PV, against C1018 steel of hardness 15-25 Rockwell C, 14-17 micro smoothness. |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 254 - 282 | °C | |
| Middle Temperature | 254 - 282 | °C | |
| Front Temperature | 254 - 282 | °C | |
| Mold Temperature | 60.0 - 93.3 | °C | |
| Injection Pressure | 68.9 - 138 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 5132-84 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Moplen HP301R | LyondellBasell Industries | PP Homopolymer | Moplen |
| YUNGSOX® PP 5018 | Formosa Polypropylene | PP Random Copolymer | YUNGSOX® PP |
| NEXT REGRIND PA66 70G33-300RG | NEXT Specialty Resins, Inc. | Nylon 66 | NEXT REGRIND |
| NuSil MED-2955 | NuSil Technology | Silicone Rubber, LSR | NuSil |