TORZEN® U4664FL NC01 is a moderately nucleated, lubricated PA66 resin suitable for injection molding, where fast crystallization and fast cycle times are required. It is lubricated internally and externally for excellent machine feed and mold release. U4664FL is also available in black. |
General Information | |
---|---|
Additive |
|
Features |
|
Agency Ratings |
|
RoHS Compliance |
|
Appearance |
|
Processing Method |
|
Physical | Nominal Value | Unit | Test Method |
---|---|---|---|
Density | 1.14 | g/cm³ | ISO 1183 |
Molding Shrinkage | ISO 294-4 | ||
Across Flow : 2.00 mm | 2.0 | % | |
Flow : 2.00 mm | 1.8 | % | |
Water Absorption (23°C, 24 hr) | 1.8 | % | ISO 62 |
Mechanical | Nominal Value | Unit | Test Method |
---|---|---|---|
Tensile Modulus | 3200 | MPa | ISO 527-2/1 |
Tensile Stress (Yield) | 83.0 | MPa | ISO 527-2/50 |
Tensile Strain | ISO 527-2 | ||
Yield | 4.0 | % | |
Break | 30 | % | |
Flexural Modulus | 3100 | MPa | ISO 178 |
Flexural Stress | 99.0 | MPa | ISO 178 |
Impact | Nominal Value | Unit | Test Method |
---|---|---|---|
Charpy Notched Impact Strength | ISO 179 | ||
-30°C | 4.5 | kJ/m² | |
23°C | 4.6 | kJ/m² | |
Charpy Unnotched Impact Strength | ISO 179 | ||
-30°C | 150 | kJ/m² | |
23°C | No Break | ||
Notched Izod Impact Strength (23°C) | 4.7 | kJ/m² | ISO 180 |
Thermal | Nominal Value | Unit | Test Method |
---|---|---|---|
Melting Temperature | 263 | °C | ISO 11357-3 |
Electrical | Nominal Value | Unit | Test Method |
---|---|---|---|
Volume Resistivity (2.00 mm) | 1.0E+10 | ohms·cm | IEC 60093 |
Electric Strength (1.00 mm) | 18 | kV/mm | IEC 60243-1 |
Comparative Tracking Index (3.00 mm) | 600 | V | IEC 60112 |
Flammability | Nominal Value | Unit | Test Method |
---|---|---|---|
Flame Rating (0.400 mm) | V-2 | UL 94 | |
Glow Wire Flammability Index | IEC 60695-2-12 | ||
0.710 mm | 960 | °C | |
1.50 mm | 960 | °C | |
3.00 mm | 960 | °C | |
Glow Wire Ignition Temperature | IEC 60695-2-13 | ||
0.710 mm | 960 | °C | |
1.50 mm | 900 | °C | |
3.00 mm | 750 | °C |
Injection | Nominal Value | Unit | |
---|---|---|---|
Drying Temperature | 80.0 | °C | |
Drying Time | 3.0 to 4.0 | hr | |
Suggested Max Moisture | 0.080 to 0.18 | % | |
Rear Temperature | 250 to 270 | °C | |
Middle Temperature | 270 to 290 | °C | |
Front Temperature | 270 to 290 | °C | |
Nozzle Temperature | 270 to 290 | °C | |
Processing (Melt) Temp | 280 to 300 | °C | |
Mold Temperature | 50.0 to 90.0 | °C | |
Back Pressure | 0.200 to 1.00 | MPa | |
Screw Speed | 75 to 180 | rpm | |
Cushion | 4.00 to 6.00 | mm | |
Vent Depth | 7.0E-3 to 0.040 | mm |
Resin Grade | Manufacturer | Category | Trademark |
---|---|---|---|
Makrolon® RW6267 X | Covestro - Polycarbonates | PC | Makrolon® |
NEMCON H PC DP113/X5 | Ovation Polymers Inc. | PC | NEMCON H |
Novalloy-S S69P1 | Daicel Polymer Ltd. | PC+ABS | Novalloy-S |
Grilon® BRZ 340 H | EMS-GRIVORY | Nylon 6 | Grilon® |
LG ABS RS657L | LG Chem Ltd. | ABS | LG ABS |