SABIC® HDPE F00952J
| Category: | HDPE, HMW , High Density (HMW) Polyethylene |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® HDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | zezUpA_SABIC-HDPE-F00952J.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SABIC® HDPE F00952J resin is a high molecular weight, high density polyethylene copolymer. The design of the product, molecular architecture and density, gives F00952J a good combination of easy extrusion and high melt strength with strong physical properties. Typical applications are thin films with excellent strength and rigidity. The material contains anti-oxidants. Typical applications SABIC® HDPE F00952J resin is typically used for blown film extrusion and production of high strength grocery sacks, shopping bags and high quality thin films for multi wall sack liners and replacement for thin paper products. Processing conditions SABIC® HDPE F00952J can be extruded on conventional HMW-HDPE equipment at melt temperaure settings between 200 and 220°C. Film properties Film properties have been measured at 15µm blown film with a BUR = 4. This product is not intended for and must not be used in any pharmaceutical/medical applications. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.952 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 190°C/2.16 kg | 0.050 | g/10 min | ISO 1133 |
| 190°C/21.6 kg | 9.5 | g/10 min | ISO 1133 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 15 | µm | |
| Elastic Modulus - MD (15 µm, Blown Film) | 1250 | MPa | ASTM D882 |
| Elastic Modulus - TD (15 µm, Blown Film) | 1500 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 15 µm, blown film | 33.0 | MPa | ASTM D882 |
| TD : Yield, 15 µm, blown film | 40.0 | MPa | ASTM D882 |
| MD : Broken, 15 µm, blown film | 66.0 | MPa | ASTM D882 |
| TD : Broken, 15 µm, blown film | 64.0 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Broken, 15 µm, blown film | 400 | % | ASTM D882 |
| TD : Broken, 15 µm, blown film | 550 | % | ASTM D882 |
| Dart Drop Impact 1(15 µm, Blown Film) | 180 | g | ASTM D1709 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 15 µm, blown film | 12 | g | ASTM D1922 |
| TD : 15 µm, blown film | 60 | g | ASTM D1922 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 125 | °C | ASTM D1525 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 200 - 220 | °C |
| Note Message | |
|---|---|
| 1 . | F50 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 281 AR 10 TFE 10 | RTP Company | Nylon 66 | RTP |
| Starflam M10004A | Eurostar Engineering Plastics | PP, Unspecified | Starflam |
| Axiall PVC 8950 | Axiall Corporation | PVC, Flexible | Axiall PVC |
| PIVINEL™ 122-RDV-LF | HELLENIC CABLES S.A. | PVC, Unspecified | PIVINEL™ |
| Sylvin 7833-95 Pink 6289 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |