MAGNUM™ 8434
| Category: | ABS , ABS Resin |
| Manufacturer: | Trinseo |
| Trademark: | MAGNUM™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | zeoZia_MAGNUM-8434.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
MAGNUM™ 8434 is a product which combines high gloss with medium-high heat performance. It is suitable for a wide range of applications. The mass (continuous process) ABS technology ensures an ABS resin that combines excellent processability with a stable light base colour that is ideal for self-colouring. Applications:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | |||
| -- | 1.05 | g/cm³ | ISO 1183/B |
| -- | 1050 | kg/m³ | ISO 1183 1 |
| Apparent Density | 0.65 | g/cm³ | ISO 60 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 13 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (220°C/10.0 kg) | 13.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow | 0.40 to 0.70 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| 3.20 mm, Injection Molded | 2100 | MPa | ISO 527-2 |
| -- | 2200 | MPa | ISO 527-2 2 |
| Tensile Stress | |||
| Yield, 3.20 mm, Injection Molded | 47.0 | MPa | ISO 527-2/50 |
| Yield, 3.20 mm, Injection Molded | 48.0 | MPa | ISO 527-2/100 |
| Yield | 45.0 | MPa | ISO 527-2 3 |
| Tensile Strain (Yield, 3.20 mm, Injection Molded) | 2.7 | % | ISO 527-2/50, ISO 527-2/100 |
| Nominal strain at break | 25 | % | ISO 527-2 4 |
| Flexural Modulus (3.20 mm, Injection Molded) | 2100 | MPa | ISO 178 |
| Flexural Stress (3.20 mm, Injection Molded) | 65.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| -30°C, Injection Molded | 10 | kJ/m² | ISO 179/1eA |
| -30°C, Injection Molded | 7.0 | kJ/m² | ISO 179/2C |
| 23°C, Injection Molded | 12 | kJ/m² | ISO 179/2C |
| 23°C, Injection Molded | 19 | kJ/m² | ISO 179/1eA |
| Charpy impact strength | ISO 179/1eU 5 | ||
| -30°C | No Break | ||
| 23°C | No Break | ||
| Notched Izod Impact Strength | ISO 180/A | ||
| -30°C, Injection Molded | 9.0 | kJ/m² | |
| 23°C, Injection Molded | 21 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 1.8 MPa, Annealed | 102 | °C | ISO 75-2/A |
| 1.8 MPa | 102 | °C | ISO 75-2 6 |
| Vicat Softening Temperature | |||
| -- | 101 | °C | ISO 306/B50 |
| 50°C/h, B (50N) | 100 | °C | ISO 306 7 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume resistivity | > 1.0E+13 | ohms·m | IEC 60093 8 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate 9(2.00 mm) | 45 | mm/min | ISO 3795 |
| Flame Rating 10 | UL 94 | ||
| 1.50 mm | HB | ||
| 3.00 mm | HB | ||
| Burning Behav. at 1.6mm nom. thickn. (1.50 mm, UL) | HB | ISO 1210 11 | |
| Carbon Emission 12 | 12.0 | µg/g | VDA 277 |
| Note Message | |
|---|---|
| 1 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 2 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 3 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 4 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 5 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 6 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 7 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 8 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 9 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| 10 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| 11 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 12 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Vinnolit® P 3468 | Vinnolit GmbH & Co. KG | PVC Homopolymer | Vinnolit® |
| UNISOFT TPE™ ST-55A-BK-3-01 | UNITED SOFT PLASTICS, Inc. | SEBS | UNISOFT TPE™ |
| Celanex® 2302 GV1/15 | Celanese Corporation | PBT | Celanex® |
| DENILEN B 3010 CB | Vamp Tech | PP, Unspecified | DENILEN |
| EPAMOULD 295A83W40 | Epaflex Polyurethanes S.R.L. | TPU-Polyester | EPAMOULD |