Latilub 57D-15T G/30
| Category: | Nylon, Unspecified , Polyamide |
| Manufacturer: | LATI S.p.A. |
| Trademark: | Latilub |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | zednnt_Latilub-57D-15T-G-30.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Self-lubricating product based on Semi-aromatic polyammide. PTFE. Glass fibres. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.55 | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | ISO 294-4 | ||
| Across Flow : 2.00 mm | 0.75 to 1.1 | % | |
| Flow : 2.00 mm | 0.35 to 0.65 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 10000 | MPa | ISO 527-2/1 |
| Tensile Stress (Break, 23°C) | 200 | MPa | ISO 527-2/5 |
| Tensile Strain (Break, 23°C) | 2.6 | % | ISO 527-2/5 |
| Coefficient of Friction | ASTM D3702 | ||
| vs. Itself - Dynamic | 0.29 | ||
| vs. Itself - Static | 0.33 | ||
| Wear Factor | 1.50E-9 | (m³/h)/(N·m·h) | ASTM D3702 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 7.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 35 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact (23°C, 3.20 mm) | 80 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 280 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 250 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 255 | °C | ISO 306/B50 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 to 100 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 320 to 340 | °C | |
| Mold Temperature | 130 to 150 | °C | |
| Injection Rate | Moderate |
| Note Message | |
|---|---|
| 1 . | at 60 Mpa of cavity pressure |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Moplen RP348N | PolyMirae | PP Random Copolymer | Moplen |
| TOLEN H022 CM | SIBUR, LLC | PP Homopolymer | TOLEN |
| Borealis PE FS1470 | Borealis AG | HDPE | Borealis PE |
| ExxonMobil™ PP7855E1 | ExxonMobil Chemical | PP Impact Copolymer | ExxonMobil™ |
| LEXAN™ EXL1443T resin | SABIC Innovative Plastics | PC | LEXAN™ |