LNP™ LUBRICOMP™ OFL36A compound
| Category: | PPS, Branched , Branched Polyphenylene Sulfide |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | zebZE5_LNPLUBRICOMPOFL36Acompound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP* OFL36 is a compound based on PPS - Branched resin containing Glass Fiber, PTFE. Added features of this material include: Internally Lubricated. Also known as: LNP* LUBRICOMP* Compound OFL-4036 Product reorder name: OFL36A |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.69 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (315°C/5.0 kg) | 10.0 - 15.0 | cm³/10min | ISO 1133 |
| Water Absorption | ISO 62 | ||
| 23°C, 24 hr | 0.020 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.030 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 11100 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 124 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 1.4 | % | ISO 527-2/5 |
| Flexural Modulus 1 | ISO 178 | ||
| -- | 9700 | MPa | ISO 178 |
| 80°C | 9300 | MPa | ISO 178 |
| 120°C | 4700 | MPa | ISO 178 |
| 150°C | 4000 | MPa | ISO 178 |
| 200°C | 3100 | MPa | ISO 178 |
| Flexural Stress | ISO 178 | ||
| -- | 216 | MPa | ISO 178 |
| 80°C | 184 | MPa | ISO 178 |
| 120°C | 114 | MPa | ISO 178 |
| 150°C | 80.0 | MPa | ISO 178 |
| 200°C | 58.0 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| With self-dynamics | 0.44 | ASTM D3702 Modified | |
| With Self-Static | 0.35 | ASTM D3702 Modified | |
| Flexural Strain at Break 2 | ISO 178 | ||
| -- | 2.4 | % | ISO 178 |
| 80°C | 2.6 | % | ISO 178 |
| 120°C | 5.2 | % | ISO 178 |
| 150°C | 5.8 | % | ISO 178 |
| 200°C | 5.7 | % | ISO 178 |
| Wear Factor - Washer | 33.0 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ISO 180/1A | ||
| -40°C 3 | 8.0 | kJ/m² | ISO 180/1A |
| 23°C 4 | 7.6 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 5 | ISO 180/1U | ||
| -40°C | 31 | kJ/m² | ISO 180/1U |
| 23°C | 32 | kJ/m² | ISO 180/1U |
| Multi-Axial Instrumented Impact Energy | 1.97 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 6(1.8 MPa, Unannealed, 64.0 mm Span) | 266 | °C | ISO 75-2/Af |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow : 23 to 60°C | 2.4E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : 23 to 60°C | 5.0E-5 | cm/cm/°C | ISO 11359-2 |
| Specific Heat | 1490 | J/kg/°C | ASTM E1269 |
| Thermal Conductivity | 0.29 | W/m/K | ASTM D5930 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 - 149 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 304 - 316 | °C | |
| Middle Temperature | 321 - 332 | °C | |
| Front Temperature | 332 - 343 | °C | |
| Processing (Melt) Temp | 316 - 321 | °C | |
| Mold Temperature | 138 - 166 | °C | |
| Back Pressure | 0.172 - 0.344 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2 mm/min |
| 3 . | 80*10*3 |
| 4 . | 80*10*4 |
| 5 . | 80*10*4 |
| 6 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Prixene® PH120I04 | POLYMAT | PP Homopolymer | Prixene® |
| SuperLite® SL550600-100 (2.5mm) | Azdel, Inc. | PP, Unspecified | SuperLite® |
| KPOL-PP K-PPC 1.50 | KPOL Chem Co. | PP Impact Copolymer | KPOL-PP |
| Rotuba CAB B9024 (5% Plasticizer) | Rotuba Extruders, Inc. | CAB | Rotuba CAB |
| LNP™ LUBRICOMP™ KP004L compound | SABIC Innovative Plastics | Acetal (POM) Copolymer | LNP™ LUBRICOMP™ |