Cevian®-V 400N
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | PlastxWorld Inc. |
| Trademark: | Cevian®-V |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | zeQv4V_Cevian--V-400N.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Cevian®-V 400N is an acrylonitrile butadiene styrene (ABS) product,. It can be processed by injection molding and is available in North America. Features include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.05 | g/cm³ | ASTM D792 |
| -- | 1.06 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | |||
| 230°C/3.8 kg | 0.60 | g/10 min | ASTM D1238 |
| 220°C/10.0 kg | 2.3 | g/10 min | ISO 1133 |
| Molding Shrinkage | |||
| Flow : 3.18mm | 0.50 - 0.80 | % | ASTM D955 |
| -- | 0.50 - 0.80 | % | ISO 294-4 |
| Water Absorption (24 hr) | 0.30 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 102 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Yield | 46.2 | MPa | ASTM D638 |
| Yield | 46.0 | MPa | ISO 527-2 |
| Flexural Modulus | |||
| -- | 2280 | MPa | ASTM D790 |
| -- | 2200 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 76.0 | MPa | ISO 178 |
| Yield | 72.4 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 3.18 mm | 140 | J/m | ASTM D256 |
| 23°C | 12 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 12.7 mm) | 115 | °C | ASTM D648 |
| Vicat Softening Temperature | |||
| -- | 130 | °C | ISO 306/A50 |
| -- | 122 | °C | ISO 306/B50 |
| -- | 124 | °C | ISO 306/B120 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm) | HB | UL 94 |
| Additional Information |
|---|
| The value listed as Mold Shrinkage, ISO 294, was tested in accordance with ISO 2577.Specific Gravity, ASTM D792, 73°F, 50% RH: 1.05Water Absorption, ASTM D570, 24 hrs, 73°F: 0.3 % |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 79.4 - 85.0 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Rear Temperature | 200 - 220 | °C | |
| Middle Temperature | 215 - 235 | °C | |
| Front Temperature | 230 - 250 | °C | |
| Processing (Melt) Temp | 240 - 260 | °C | |
| Mold Temperature | 48.9 - 60.0 | °C | |
| Injection Pressure | 34.5 - 103 | MPa | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 0.689 - 2.07 | MPa | |
| Screw Speed | 60 - 80 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ALCOM® PC 740/4 WT1140-03LD | ALBIS PLASTIC GmbH | PC | ALCOM® PC |
| ASI POLYPROPYLENE 1498-01 | A. Schulman Inc. | PP Impact Copolymer | ASI POLYPROPYLENE |
| COSMOPLENE® W531 | TPC, The Polyolefin Company (Singapore) Pte Ltd | PP, Unspecified | COSMOPLENE® |
| DIOSHY® VP-895 | DIOSHY Co.,Ltd. | TPV | DIOSHY® |
| Hifax TYC 1168P E C11538 | LyondellBasell Industries | PP Copolymer | Hifax |