Order Products : sales@su-jiao.com
KumhoSunny PC/ASA HSC7045
| Category: | ASA+PC , Acrylonitrile Styrene Acrylate + PC |
| Manufacturer: | Shanghai KumhoSunny Plastics Co., Ltd. |
| Trademark: | KumhoSunny PC/ASA |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ze8qUg_KumhoSunny-PC-ASA-HSC7045.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| HSC7045 is a high flow PC/ASA resin. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| UL File Number |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.11 | g/cm³ | ASTM D792 |
| -- | 1.12 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/10.0 kg) | 20 | g/10 min | ASTM D1238 |
| Molding Shrinkage | |||
| Flow | 0.50 to 0.70 | % | ASTM D955 |
| -- | 0.50 to 0.70 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 50.0 | MPa | ASTM D638, ISO 527-2/50 |
| Tensile Elongation (Break) | 60 | % | ASTM D638 |
| Flexural Modulus | |||
| -- | 2100 | MPa | ASTM D790 |
| -- 1 | 2000 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 75.0 | MPa | ASTM D790 |
| -- 2 | 65.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 3 | ISO 179 | ||
| -30°C | 23 | kJ/m² | |
| 23°C | 48 | kJ/m² | |
| Charpy Unnotched Impact Strength 4(23°C) | No Break | ISO 179 | |
| Notched Izod Impact | |||
| 3.20 mm | 550 | J/m | ASTM D256 |
| 23°C 5 | 45 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 100 | °C | ASTM D648, ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 112 | °C | ASTM D1525 6 |
| -- | 110 | °C | ISO 306/B50 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 to 100 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Suggested Max Moisture | < 0.020 | % | |
| Rear Temperature | 220 to 230 | °C | |
| Middle Temperature | 230 to 240 | °C | |
| Front Temperature | 250 to 260 | °C | |
| Nozzle Temperature | 240 to 250 | °C | |
| Processing (Melt) Temp | 240 to 260 | °C | |
| Mold Temperature | 50.0 to 80.0 | °C | |
| Back Pressure | 0.300 to 1.00 | MPa | |
| Screw Speed | 30 to 70 | rpm |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 4J |
| 4 . | 4J |
| 5 . | 5.5J |
| 6 . | Rate B (120°C/h) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Rainmaker Polypropylene MCCPCC20 | Rainmaker Polymers LLC | PP Copolymer | Rainmaker Polypropylene |
| ALCOM® PC 740/4 WT1140-03LD | ALBIS PLASTIC GmbH | PC | ALCOM® PC |
| DURACON® JW-03 | Polyplastics Co., Ltd. | Acetal (POM) Copolymer | DURACON® |
| INLUBE PA12GF15TF15 | Infinity LTL Engineered Compounds | Nylon 12 | INLUBE |
| REV Materials 8003 | REV Materials | Polyolefin, Unspecified | REV Materials |