TOTAL Polyethylene Lumicene® M 3427
| Category: | MDPE , Medium Density Polyethylene |
| Manufacturer: | TOTAL Refining & Chemicals |
| Trademark: | TOTAL Polyethylene |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ze22n7_TOTAL-Polyethylene-Lumicene-M-3427.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Lumicene® mPE M 3427 is a second generation metallocene based Polyethylene with hexene as comonomer. Lumicene® mPE M 3427 can be processed at high output rates with low extrusion pressure, low neck-in, excellent drawability and good gauge control in comparison with conventional LLDPE and first generation metallocene based polyethylene. The combination of these features combined with excellent optical properties brings a significant downgauging potential. Lumicene® mPE M 3427 is suited for many applications in the field of consumer, food and hygiene packaging such as hygiene film, stretch wrap (non cling layer) and lamination. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.934 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 3.1 | g/10 min | ISO 1133 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 20 | µm | |
| Tensile Stress | ISO 527-3 | ||
| MD : Yield, 20 µm, Cast Film | 12.0 | MPa | |
| TD : Yield, 20 µm, Cast Film | 11.5 | MPa | |
| MD : Break, 20 µm, Cast Film | 39.0 | MPa | |
| TD : Break, 20 µm, Cast Film | 27.0 | MPa | |
| Tensile Elongation | ISO 527-3 | ||
| MD : Break, 20 µm, Cast Film | 480 | % | |
| TD : Break, 20 µm, Cast Film | 590 | % | |
| Dart Drop Impact (20 µm, Cast Film) | 53 | g | ISO 7765-1 |
| Elmendorf Tear Strength 1 | ISO 6383-2 | ||
| MD : 20.0 µm | 21.0 | kN/m | |
| TD : 20.0 µm | 115.0 | kN/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 120 | °C | ISO 306 |
| Melting Temperature | 123 | °C | ISO 11357-3 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 20.0 µm, Cast Film) | 86 | ASTM D2457 | |
| Haze (20.0 µm, Cast Film) | 2.3 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 240 to 280 | °C | |
| Take-Off Roll | 20.0 to 60.0 | °C |
| Note Message | |
|---|---|
| 1 . | Cast Film |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Xuchuan XCS-3030L | Xuchuan Chemical (Suzhou) Co., Ltd | PUR, Unspecified | Xuchuan |
| Exelene® LLDPE 2400 | Montachem International, Inc. | LLDPE | Exelene® LLDPE |
| LNP™ THERMOCOMP™ JF004E compound | SABIC Innovative Plastics | PESU | LNP™ THERMOCOMP™ |
| LUVOCOM® 1301-8517 | Lehmann & Voss & Co. | PPS | LUVOCOM® |
| Luranyl® KR 2403 G2 TW 26343 | ROMIRA GmbH | PPE+PS | Luranyl® |