LG PS 60HRI
| Category: | PS (HIPS) , High Impact Polystyrene |
| Manufacturer: | LG Chem Ltd. |
| Trademark: | LG PS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | zdubEI_LG-PS-60HRI.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LG PS 60HRI is a High Impact Polystyrene material. It is available in Asia Pacific, Europe, Latin America, or North America for injection molding. Important attributes of LG PS 60HRI are:
Typical application of LG PS 60HRI: Appliances |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Multi-Point Data |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.03 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 200°C/5.0 kg | 6.0 | g/10 min | |
| 220°C/10.0 kg | 65 | g/10 min | |
| 230°C/3.8 kg | 15 | g/10 min |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 99 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1(3.20 mm) | 1780 | MPa | ASTM D638 |
| Tensile Strength 2(Yield, 3.20 mm) | 26.5 | MPa | ASTM D638 |
| Tensile Elongation 3 | ASTM D638 | ||
| Yield, 3.20 mm | 5.0 | % | |
| Break, 3.20 mm | 62 | % | |
| Flexural Modulus 4(3.20 mm) | 2130 | MPa | ASTM D790 |
| Flexural Strength 5(3.20 mm) | 42.2 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -30°C, 3.20 mm | 59 | J/m | |
| -30°C, 6.40 mm | 49 | J/m | |
| 23°C, 3.20 mm | 130 | J/m | |
| 23°C, 6.40 mm | 88 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 6.40 mm | 91.0 | °C | |
| 1.8 MPa, Unannealed, 6.40 mm | 82.0 | °C | |
| Vicat Softening Temperature | 90.0 | °C | ASTM D1525 6 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.60 mm | HB | ||
| 3.20 mm | HB |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Minimum Moisture Content | 0.010 | % | |
| Rear Temperature | 170 to 190 | °C | |
| Middle Temperature | 180 to 200 | °C | |
| Front Temperature | 190 to 210 | °C | |
| Nozzle Temperature | 190 to 220 | °C | |
| Processing (Melt) Temp | 190 to 220 | °C | |
| Mold Temperature | 40.0 to 70.0 | °C | |
| Back Pressure | 29.4 to 58.8 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 1.0 mm/min |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| 4 . | 15 mm/min |
| 5 . | 15 mm/min |
| 6 . | Rate A (50°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Spartech Polycom SCR7-7022 | Spartech Polycom | PC | Spartech |
| Celstran® PA66-GF60-02-Natural | Celanese Corporation | Nylon 66 | Celstran® |
| Elvacite® 2042 | Lucite International Inc. | Acrylic (PMMA) | Elvacite® |
| Hypro® PPH-GF10 NATURAL | Entec Polymers | PP Homopolymer | Hypro® |
| LNP™ LUBRICOMP™ RP004 compound | SABIC Innovative Plastics | Nylon 66 | LNP™ LUBRICOMP™ |