Lucky Enpla LGF3110R
| Category: | PC+PBT , Polycarbonate + PBT |
| Manufacturer: | Lucky Enpla Co LTD |
| Trademark: | Lucky Enpla |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | zdI0tA_Lucky-Enpla-LGF3110R.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Lucky Enpla LGF3110R is a polycarbonate + polybutene terephthalate (PC + PBT) product, which contains a 11% glass fiber reinforced material. It can be processed by injection molding and is available in North America, Europe or the Asia-Pacific region. Typical application areas are: automotive industry. Features include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.29 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.70 - 1.0 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | 82.4 | MPa | ASTM D638 |
| Flexural Modulus 2 | 3870 | MPa | ASTM D790 |
| Flexural Strength 3 | 127 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Unnotched Izod Impact | ASTM D256 | ||
| 3.18 mm | 69 | J/m | ASTM D256 |
| 6.35 mm | 59 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 115 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 - 90.0 | °C | |
| Drying Time | 2.0 - 3.0 | hr | |
| Rear Temperature | 240 - 270 | °C | |
| Middle Temperature | 250 - 270 | °C | |
| Front Temperature | 260 - 280 | °C | |
| Nozzle Temperature | 260 - 280 | °C | |
| Mold Temperature | 30.0 - 60.0 | °C | |
| Back Pressure | 0.490 - 1.47 | MPa | |
| Screw Speed | 40 - 70 | rpm |
| Injection instructions |
|---|
| Resin Temperature: 260-280°CInjection Pressure (1st Pressure): 800-1200 kg/cm²Injection Pressure (2nd Pressure): 500-800 kg/cm² |
| Note Message | |
|---|---|
| 1 . | 10 mm/min |
| 2 . | 3.0 mm/min |
| 3 . | 3.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shin-Etsu RTV KE-347TUV | Shin-Etsu Silicones of America | Silicone Rubber, RTV-1 | Shin-Etsu RTV |
| XYRON™ 1000H | Asahi Kasei Chemicals Corporation | PPE+PS | XYRON™ |
| Network Polymers SAN 290 | Network Polymers, Inc. | SAN | Network Polymers SAN |
| Karina IVORY PVC COMPOUND KAPU 5535/1-Y(***) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Polifil® Nylon 625 | The Plastics Group | Nylon 66 | Polifil® Nylon |