Order Products : sales@su-jiao.com
Pro-fax SV152
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Pro-fax |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | zdHxBY_Pro-fax-SV152.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Pro-fax SV152 nucleated very high impact polypropylene copolymer is available in pellet form. This resin is typically used in general extrusion and blow molding applications and offers excellent cold temperature impact resistance. An ASTM and ISO-based versions of the technical datasheet are available for Pro-fax SV152 For regulatory compliance information see Pro-fax SV152 Product Stewardship Bulletin (PSB). |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 0.898 | g/cm³ | ASTM D792B |
| -- | 0.900 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 1.4 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Yield 1 | 24.1 | MPa | ASTM D638 |
| Yield, 23°C | 24.0 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield | 9.0 | % | ASTM D638 |
| Yield, 23°C | 8.0 | % | ISO 527-2 |
| Flexural Modulus | |||
| 1% Secant 2 | 1140 | MPa | ASTM D790A |
| 23°C | 1180 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -40°C | 4.2 | kJ/m² | |
| 23°C | 85 | kJ/m² | |
| Notched Izod Impact | |||
| 23°C | No Break | ASTM D256A | |
| -40°C | 4.7 | kJ/m² | ISO 180 |
| 23°C | 64 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 90.6 | °C | ASTM D648 |
| 0.45 MPa, Unannealed | 78.0 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 49.0 | °C | ISO 75-2/A |
| Note Message | |
|---|---|
| 1 . | 51 mm/min |
| 2 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POPELEN HIP-373 | Lotte Chemical Corporation | PP Impact Copolymer | POPELEN |
| RTP ESD 300 EM FR A | RTP Company | PC | RTP |
| Staramide BG6ST01 | Eurostar Engineering Plastics | Nylon 6 | Staramide |
| Advanced Composites ADX-2001 | Advanced Composites, Inc. | PP, Unspecified | Advanced Composites |
| TECHNYL® C 216 V45 NATURAL | Solvay Engineering Plastics | Nylon 6 | TECHNYL® |