EcoBlend® HML5150
| Category: | PLA+PMMA , Polylactic Acid + PMMA |
| Manufacturer: | Shanghai KumhoSunny Plastics Co., Ltd. |
| Trademark: | EcoBlend® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | zdHo89_EcoBlend-HML5150.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| HML5150 is a kind of appending 50%~60% biological base plastic environmental PLA/PMMA resin.HML5150 has excellent mechanical properties and excellent transpranet properties.HML5150 is mainly used in window of OA, ornament of TV set,etc. |
| General Information | |
|---|---|
| Features |
|
| UL File Number |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.21 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 190°C/2.16 kg | 6.9 | g/10 min | |
| 240°C/5.0 kg | 6.9 | g/10 min | |
| Molding Shrinkage - Flow | 0.50 to 0.70 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 70.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 8.0 | % | ASTM D638 |
| Flexural Modulus | 3200 | MPa | ASTM D790 |
| Flexural Strength | 75.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | 30 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 64.5 | °C | ASTM D648 |
| Vicat Softening Temperature | 67.5 | °C | ASTM D1525 1 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Biobased Content | 50 to 60 | % | |
| CSA File No. | LS 66457 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 90.0 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 190 to 200 | °C | |
| Middle Temperature | 210 to 220 | °C | |
| Front Temperature | 220 to 230 | °C | |
| Nozzle Temperature | 215 to 225 | °C | |
| Processing (Melt) Temp | 220 to 230 | °C | |
| Mold Temperature | 60.0 to 80.0 | °C | |
| Back Pressure | 1.00 to 5.00 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | Rate B (120°C/h) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 2587 FR | RTP Company | PC+ABS | RTP |
| Sylvin 7606-80 Clear | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| TRISTAR® PC-10R-(V6) | Polymer Technology and Services, LLC | PC | TRISTAR® |
| 3M™ Dyneon™ Fluoroelastomer FG 5690Q | 3M Advanced Materials Division | Fluorelastomer | 3M™ Dyneon™ Fluoroelastomer |
| KOPLA PA66 KDG1030F | KOPLA Co., Ltd. | Nylon 66 | KOPLA PA66 |