Sumitomo PE FS253S
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Sumitomo Chemical Asia |
| Trademark: | Sumitomo PE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | zd5GTF_Sumitomo-PE-FS253S.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Applications For grocery bag, garment packaging, agriculture film, and other general purpose film applications. Characteristics High strength film with excellent processability, high slip and antiblocking properties. For higher transparency, blending with LDPE is recommended. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.922 | g/cm³ | ASTM D792A |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 2.2 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction | ASTM D1894 | ||
| With self-dynamics | 0.080 | ASTM D1894 | |
| With Self-Static | 0.11 | ASTM D1894 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| secant modulus | ASTM D882 | ||
| 1% secant, MD | 205 | MPa | ASTM D882 |
| 0.05% to 1.05%, TD | 255 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Fracture | 35.0 | MPa | ASTM D882 |
| TD : Fracture | 30.0 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Fracture | 770 | % | ASTM D882 |
| TD : Fracture | 930 | % | ASTM D882 |
| Dart Drop Impact | 90 | g | ASTM D1709 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD | 130 | g | ASTM D1922 |
| TD | 350 | g | ASTM D1922 |
| Blocking Load | 14 | g | ASTM D3354 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature | 122 | °C | DSC |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°) | 55 | ASTM D2457 | |
| Haze | 15 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 160 - 200 | °C |
| Extrusion instructions |
|---|
| Blow-up Ratio: 2 to 3 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® C4830 | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| SABIC® PP 513A | Saudi Basic Industries Corporation (SABIC) | PP Homopolymer | SABIC® PP |
| Dugdale PVC Rigid Extrusion White Compound | Dugdale Plc | PVC, Rigid | Dugdale PVC |
| POLYFLAM® RPP 1021 | A. Schulman Inc. | PP, Unspecified | POLYFLAM® |
| TECACOMP® PBT TC white 4038 | Ensinger GmbH | PBT | TECACOMP® |