Electrafil® J-1/CF/30/TF/13/SI/2
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Techmer Engineered Solutions |
| Trademark: | Electrafil® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | zcUaye_Electrafil-J-1-CF-30-TF-13-SI-2.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Electrafil®J-1/CF/30/TF/13/SI/2 is a polyamide 66 (nylon 66) product containing a 30% carbon fiber reinforced material. It can be processed by injection molding and is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific. Electrafil®The application fields of J-1/CF/30/TF/13/SI/2 include packaging, engineering/industrial accessories, automobile industry, commercial/office supplies and conveyor belts. Features include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.36 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 0.10 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.60 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (23°C) | 193 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 2.5 | % | ASTM D638 |
| Flexural Modulus (23°C) | 15200 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 276 | MPa | ASTM D790 |
| Compressive Strength | 172 | MPa | ASTM D695 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 96 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 260 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 252 | °C | ASTM D648 |
| CLTE - Flow | 1.4E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 5.5E+2 | ohms | ASTM D257 |
| Volume Resistivity | 5.5 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Additional Information |
|---|
| Compressive Strength, ASTM D695, 73°F: 25000 psiSurface Resistivity, ASTM D257: 1E2-1E3 ohmVolume Resistivity, ASTM C611: 1-10 ohm-cm |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.10 | % | |
| Rear Temperature | 288 - 299 | °C | |
| Middle Temperature | 293 - 304 | °C | |
| Front Temperature | 282 - 293 | °C | |
| Nozzle Temperature | 277 - 288 | °C | |
| Processing (Melt) Temp | 293 - 304 | °C | |
| Mold Temperature | 79.4 - 104 | °C | |
| Injection Rate | Moderate | ||
| Back Pressure | 0.345 | MPa |
| Injection instructions |
|---|
| Screw Speed: MediumRecommendations for Molding and Tool Conditions: Well vented moldMoisture Content, as received: Product is packaged at 0.2% or less. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| THERMOLAST® K TC4PAN (Series: AD/PA) | KRAIBURG TPE | TPE | THERMOLAST® K |
| Xuchuan A-9088A/B-6088A | Xuchuan Chemical (Suzhou) Co., Ltd | TPU-Polyester | Xuchuan |
| AVALON® 75 ABX | Huntsman Corporation | TPU-Polyester | AVALON® |
| Estane® 2103-80AE TPU | Lubrizol Advanced Materials, Inc. | TPU-Polyether | Estane® |
| Deprene 101-87 | Shanghai Lin Gen Rubber Materials Co., Ltd. | PP+EPDM | Deprene |