Spartech PS SP-2010
| Category: | PS (HIPS) , High Impact Polystyrene |
| Manufacturer: | Spartech Plastics |
| Trademark: | Spartech |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | zcI5l6_Spartech-PS-SP-2010.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| SP-2010 is engineered from the toughest polystyrene resins to provide a superior balance of processability, stiffness, deep-draw formability, and high impact strength. |
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.04 | g/cm³ | ASTM D792 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 95 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1650 | MPa | ASTM D638 |
| Tensile Strength (Yield) | 24.1 | MPa | ASTM D638 |
| Flexural Modulus | 1910 | MPa | ASTM D790 |
| Flexural Strength | 47.6 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 110 | J/m | ASTM D256 |
| Dart Drop Impact (23°C) | 14.1 | J | ASTM D3029 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 85.0 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Optical | Nominal Value | Test Method | |
|---|---|---|---|
| Gardner Gloss | 70 | ASTM D523 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SUMIPEX® MM | Sumitomo Chemical Co., Ltd. | Acrylic (PMMA) | SUMIPEX® |
| ULTEM™ 9075 resin | SABIC Innovative Plastics | PEI | ULTEM™ |
| Generic TPO - Mineral | Generic | TPO | Generic |
| Huafon JF-S-AH7035C | Huafon Group Co., Ltd. | PUR, Unspecified | Huafon |
| Magnobond 2004 | Magnolia Plastics, Inc. | Epoxy | Magnobond |