Retpol® CA 24 HS UV2 AS
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | PolyPacific Pty. Ltd. |
| Trademark: | Retpol® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | zcCOTK_Retpol-CA-24-HS-UV2-AS.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| POLYCOMP CA 24 HS UV2 AS is an unfilled high flow polypropylene copolymer compound. It is particularly suited to mouldings with relatively long flow lengths or thin walled sections. It has been heat and light stabilized to meet automotive interior requirements. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.898 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 23 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.00 mm) | 1.4 to 1.9 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale, 3.00 mm) | 82 | ASTM D785 | |
| Durometer Hardness | ASTM D2240 | ||
| Shore D, 3.00 mm | 71 | ||
| Shore D, 15 sec, 3.00 mm | 61 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(3.00 mm) | 23.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.00 mm) | 500 | % | ASTM D638 |
| Flexural Modulus (3.00 mm) | 1180 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.00 mm) | 72 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.00 mm) | 1500 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed, 3.00 mm) | 101 | °C | ASTM D648 |
| CLTE - Flow (-30 to 30°C, 3.00 mm) | 1.0E-4 | cm/cm/°C | ASTM D696 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Suggested Max Regrind | 10 | % | |
| Processing (Melt) Temp | 200 to 260 | °C | |
| Mold Temperature | 20.0 to 60.0 | °C | |
| Injection Rate | Moderate-Fast |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Moplen EP2X30F | Shazand (Arak) Petrochemical Corporation | PP Random Copolymer | Moplen |
| TEREZ PA 6 7510 GF 10 MF 30 | TER HELL PLASTIC GMBH | Nylon 6 | TEREZ PA 6 |
| UmaPET MHLO | Ester Industries Ltd. | PET | UmaPET |
| Karina CLEAR PVC COMPOUND -E 80/297-IS-RG | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Karina MBPEB WHITE 1000/00851-IE | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |