Fortron® 6160B4
| Category: | PPS , Polyphenylene Sulfide |
| Manufacturer: | Celanese Corporation |
| Trademark: | Fortron® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | zcBOs4_Fortron-6160B4.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Fortron 6160B4 has excellent heat and chemical resistance as well as good electrical properties. This product is inherently flame-retardant and offers high hardness and rigidity. 6160B4 has demonstrated excellent performance in hot runner systems and superior contact corrosion resistance. Applications include electronic components (i.e. molded in lead frames, contacts or pins). |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.90 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | ||
| Vertical flow direction | 0.30 - 0.70 | % | ISO 294-4 |
| Flow direction | 0.20 - 0.60 | % | ISO 294-4 |
| Water Absorption (Saturation, 23°C) | 0.020 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 100 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 17300 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Break) | 145 | MPa | ISO 527-2/1A/5 |
| Tensile Strain (Break) | 1.0 | % | ISO 527-2/1A/5 |
| Flexural Modulus (23°C) | 16700 | MPa | ISO 178 |
| Flexural Stress 1 | 220 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 7.0 | kJ/m² | ISO 179/1eA |
| 23°C | 7.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 27 | kJ/m² | ISO 179/1eU |
| 23°C | 27 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact | ISO 180/1A | ||
| -30°C | 7.0 | kJ/m² | ISO 180/1A |
| 23°C | 7.0 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 1.8 MPa, not annealed | 270 | °C | ISO 75-2/A |
| 8.0 MPa, not annealed | 220 | °C | ISO 75-2/C |
| Glass Transition Temperature 2 | 90.0 | °C | ISO 11357-2 |
| Melting Temperature 3 | 280 | °C | ISO 11357-3 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
| Dielectric Strength | 26 | kV/mm | IEC 60243-1 |
| Relative Permittivity (1 MHz) | 4.90 | IEC 60250 | |
| Dissipation Factor (1 MHz) | 1.0E-3 | IEC 60250 | |
| Comparative Tracking Index | 175 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.810 mm | V-0 | UL 94 | |
| 1.50 mm | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 130 - 140 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Hopper Temperature | 20.0 - 30.0 | °C | |
| Rear Temperature | 290 - 300 | °C | |
| Middle Temperature | 310 - 320 | °C | |
| Front Temperature | 330 - 340 | °C | |
| Nozzle Temperature | 310 - 330 | °C | |
| Processing (Melt) Temp | 330 - 340 | °C | |
| Mold Temperature | 140 - 160 | °C | |
| Injection Pressure | 50.0 - 100 | MPa | |
| Injection Rate | Fast | ||
| Holding Pressure | 30.0 - 70.0 | MPa | |
| Back Pressure | 0.00 - 3.00 | MPa |
| Injection instructions |
|---|
| Manifold Temperature: 330 to 340°CZone 4 Temperature: 330 to 340°CFeed Temperature: 60 to 80°C |
| Note Message | |
|---|---|
| 1 . | Break |
| 2 . | 10°C/min |
| 3 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RJM TPS-G 45A | RJM International, Inc. | TPE | RJM |
| Sylvin 8732-85 White 1151 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Karina BLACK PVC COMPOUND -E CAK 65/48/ 1-CS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| POLYfill PPH GK8040 | Polykemi AB | PP Homopolymer | POLYfill |
| TAFMER™ DF810 | Mitsui Chemicals, Inc. | PAO | TAFMER™ |