Laramid G/60
| Category: | PPA , Polyphthalamide |
| Manufacturer: | LATI S.p.A. |
| Trademark: | Laramid |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | zc0xZl_Laramid-G-60.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Compound based on Semi-aromatic polyammide. Glass fibres. Very good thermal properties. Good chemical resistance. Low moisture absorption. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.78 | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | ISO 294-4 | ||
| Across Flow : 2.00 mm | 0.50 to 0.80 | % | |
| Flow : 2.00 mm | 0.15 to 0.45 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | ISO 527-2/1 | ||
| 23°C | 26500 | MPa | |
| 60°C | 19500 | MPa | |
| 90°C | 14500 | MPa | |
| 120°C | 11000 | MPa | |
| 150°C | 8500 | MPa | |
| Tensile Stress | ISO 527-2/5 | ||
| Break, 23°C | 290 | MPa | |
| Break, 60°C | 230 | MPa | |
| Break, 90°C | 200 | MPa | |
| Break, 120°C | 180 | MPa | |
| Break, 150°C | 110 | MPa | |
| Tensile Strain | ISO 527-2/5 | ||
| Break, 23°C | 2.6 | % | |
| Break, 60°C | 3.2 | % | |
| Break, 90°C | 4.0 | % | |
| Break, 120°C | 6.0 | % | |
| Break, 150°C | 7.0 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 15 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 90 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact (23°C) | 140 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 290 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 280 | °C | ISO 75-2/A |
| Continuous Use Temperature 2 | 140 | °C | |
| Vicat Softening Temperature | 280 | °C | ISO 306/B50 |
| CLTE - Flow (30 to 100°C) | 3.0E-6 | cm/cm/°C | ASTM D696 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.750 mm | HB | ||
| 1.50 mm | HB | ||
| 3.00 mm | HB | ||
| Glow Wire Flammability Index | IEC 60695-2-12 | ||
| 1.00 mm | 750 | °C | |
| 2.00 mm | 750 | °C | |
| Oxygen Index | 42 | % | ASTM D2863 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 to 130 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 310 to 340 | °C | |
| Mold Temperature | 150 to 170 | °C | |
| Injection Rate | Moderate |
| Note Message | |
|---|---|
| 1 . | at 60 MPa of cavity pressure |
| 2 . | 20,000 hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SumiDurez 111 | SumiDurez Singapore Pte Ltd | Phenolic | SumiDurez |
| Axiall PVC 8918 | Axiall Corporation | PVC, Flexible | Axiall PVC |
| Hanwha Total PP HJ492 | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP, Unspecified | Hanwha Total PP |
| INLUBE INX-STY-11085 | Infinity LTL Engineered Compounds | PS (GPPS) | INLUBE |
| Petrotene® PP B3 T40 HS NTLA013 PH343 | Petropol Industry and Trade of Polymers LTDA | PP Copolymer | Petrotene® PP |