Description General Purpose, Soft Touch Application Automotive Interior |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 100 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A, 23°C, Injection Molded) | 85 to 91 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Break, 23°C, 2.00 mm, Injection Molded) | 8.34 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 23°C, 2.00 mm, Injection Molded) | 300 | % | ASTM D638 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -40°C, 6.40 mm, Injection Molded | No Break | ||
| 23°C, 6.40 mm, Injection Molded | No Break |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -60.0 | °C | ASTM D746 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 60.0 to 90.0 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Rear Temperature | 180 to 200 | °C | |
| Middle Temperature | 120 to 220 | °C | |
| Front Temperature | 200 to 230 | °C | |
| Nozzle Temperature | 200 to 240 | °C | |
| Processing (Melt) Temp | 200 to 240 | °C | |
| Mold Temperature | 40.0 to 60.0 | °C | |
| Back Pressure | 29.4 to 58.8 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 200 mm/min |
| 2 . | 200 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ravago Compounds HM-230 | Ravago Manufacturing Americas, LLC | LLDPE | Ravago Compounds |
| Wellamid® GF33-66/6 XE-BK167A | Wellman Engineering Resins | Nylon 66/6 | Wellamid® |
| VAMPLEN A 0023 O V2 | Vamp Tech | PP Homopolymer | VAMPLEN |
| Karina WHITE PVC COMPOUND 801-10/ 95-A-ERYB (**) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Luxus PP 16052 | Luxus Limited | PP, Unspecified | Luxus PP |