Salflex 805C
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | Salflex Polymers Ltd. |
| Trademark: | Salflex |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | zbaa1F_Salflex-805C.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Salflex 805C is a polypropylene copolymer (PP Copoly) product, which contains a 5.0% glass fiber reinforced material. It can be processed by blow molding or extrusion and is available in North America. Typical application areas are: automotive industry. The main characteristics are: impact resistance. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.930 | g/cm³ | ISO 1183/A |
| Melt Mass-Flow Rate (MFR) | 1.4 | g/10 min | ISO 1133 |
| Molding Shrinkage | 0.80 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 29.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 7.0 | % | ISO 527-2 |
| Flexural Modulus | 1330 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 17 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 109 | °C | ISO 75-2/A |
| Additional Information |
|---|
| Ash Content, ISO 3451/1A: 5.1% |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 - 100 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Cylinder Zone 1 Temp. | 180 - 210 | °C | |
| Cylinder Zone 2 Temp. | 180 - 220 | °C | |
| Cylinder Zone 3 Temp. | 180 - 220 | °C | |
| Cylinder Zone 4 Temp. | 180 - 220 | °C | |
| Melt Temperature | 180 - 215 | °C | |
| Die Temperature | 180 - 230 | °C |
| Extrusion instructions |
|---|
| Blow Molding Mold Temperature: 30 to 70°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MALECCA K-700 | Denka Company Limited | ABS | MALECCA |
| Huafon JF-P-9871 / JF-I-9818 (midsole) | Huafon Group Co., Ltd. | PUR-Ester | Huafon |
| LNP™ THERMOCOMP™ LF006 compound | SABIC Innovative Plastics | PEEK | LNP™ THERMOCOMP™ |
| Polifor® 25 CF/20 H NERO | SO.F.TER. SPA | PP Homopolymer | Polifor® |
| POCAN® BF 4222 000000 | LANXESS Corporation | PBT | POCAN® |