Fiberfil® PP-60/TC/13 BL8860
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Fiberfil® Engineered Plastics Inc. |
| Trademark: | Fiberfil® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | zbVf8B_Fiberfil-PP-60-TC-13-BL8860.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Fiberfil®PP-60/TC/13 BL8860 is a polypropylene homopolymer (PP Homopoly) material, which contains 13% talc filler. This product is available in North America,. Fiberfil®The main features of PP-60/TC/13 BL8860 are:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.01 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 13 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | ASTM D955 | ||
| 3.18 mm | 1.3 | % | ASTM D955 |
| 6.35 mm | 2.0 | % | ASTM D955 |
| 12.7 mm | 3.0 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.030 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 90 - 95 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 2340 | MPa | ASTM D638 |
| Tensile Strength (23°C) | 33.8 | MPa | ASTM D638 |
| Tensile Elongation (Yield, 23°C) | 25 | % | ASTM D638 |
| Flexural Modulus - Tangent (23°C) | 2210 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 48.3 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 27 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 132 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 85.0 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 76.7 | °C | |
| Drying Time | 2.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 199 - 210 | °C | |
| Middle Temperature | 204 - 227 | °C | |
| Front Temperature | 182 - 199 | °C | |
| Nozzle Temperature | 182 - 193 | °C | |
| Processing (Melt) Temp | 199 - 232 | °C | |
| Mold Temperature | 32.2 - 71.1 | °C | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 0.00 - 0.689 | MPa |
| Injection instructions |
|---|
| Screw speed: Medium to Fast |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 199 X 124797 A | RTP Company | PP, Unspecified | RTP |
| Yuyao PA 011BG20 | Yuyao Tenglong Plastics Co., Ltd. | Nylon 66/6 | Yuyao PA |
| ELITE™ 5210 G | The Dow Chemical Company | EPE | ELITE™ |
| Kingfa PBT RG302 | Kingfa | PBT | Kingfa PBT |
| Plaslube® ABS/PBT BK | Techmer Engineered Solutions | ABS+PBT | Plaslube® |