Panlite® GN-3430R
| Category: | PC , Polycarbonate |
| Manufacturer: | TEIJIN LIMITED |
| Trademark: | Panlite® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | zb3Ln9_Panlite-GN-3430R.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Glass fiber reinforced grades-30% Glass fiber, Flame resistant grade |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.44 | g/cm³ | ISO 1183 |
| Molding Shrinkage | Internal Method | ||
| Across Flow : 4.00 mm | 0.30 to 0.50 | % | |
| Flow : 4.00 mm | 0.020 to 0.20 | % | |
| Water Absorption (23°C, 24 hr) | 0.12 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 8200 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 105 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 2.0 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 7300 | MPa | ISO 178 |
| Flexural Stress 2 | 155 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 10 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength | 35 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 151 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 148 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 153 | °C | ISO 306/B50 |
| CLTE | ISO 11359-2 | ||
| Flow | 2.0E-5 | cm/cm/°C | |
| Transverse | 6.0E-5 | cm/cm/°C | |
| RTI Elec (1.50 mm) | 130 | °C | UL 746 |
| RTI Imp (1.50 mm) | 120 | °C | UL 746 |
| RTI Str (1.50 mm) | 130 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
| Electric Strength 3 | 35 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | ||
| 100 Hz | 3.50 | ||
| 1 MHz | 3.50 | ||
| Dissipation Factor | IEC 60250 | ||
| 100 Hz | 1.0E-3 | ||
| 1 MHz | 9.0E-3 | ||
| Comparative Tracking Index | 175 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.430 mm | V-2 | ||
| 1.50 mm | V-0 | ||
| Glow Wire Flammability Index | IEC 60695-2-12 | ||
| 1.00 mm | 960 | °C | |
| 3.00 mm | 960 | °C | |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | ||
| 1.00 mm | 900 | °C | |
| 3.00 mm | 875 | °C |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | short time test |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 2183 LF | RTP Company | PEI | RTP |
| SLOVAMID® 66 GF 50 HTS | Plastcom | Nylon 66 | SLOVAMID® 66 |
| Thermoset Plastics UR-127 | Thermoset, Lord Chemical Products | PUR, Unspecified | Thermoset Plastics |
| KRATON® D1114 P | Kraton Polymers LLC | SIS | KRATON® |
| LNP™ LUBRILOY™ UA200A compound | SABIC Innovative Plastics | PPA | LNP™ LUBRILOY™ |