WPP PP PPC1CF2-Black
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | Washington Penn Plastic Co. Inc. |
| Trademark: | WPP PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | zb3EGH_WPP-PP-PPC1CF2-Black.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
WPP PP PPC1CF2-Black is a polypropylene copolymer (PP Copoly) product, which contains 20% calcium carbonate filler. It can be processed by sheet extrusion molding and is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific. Typical application areas are: automotive industry. Features include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.04 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 1.8 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus - 2% Secant 1 | 239 | MPa | ASTM D638 |
| Tensile Strength | ASTM D638 | ||
| Yield 2 | 19.0 | MPa | ASTM D638 |
| Yield 3 | 20.0 | MPa | ASTM D638 |
| Tensile Elongation | ASTM D638 | ||
| Fracture 4 | 810 | % | ASTM D638 |
| Fracture 5 | 930 | % | ASTM D638 |
| Flexural Modulus 6 | 746 | MPa | ASTM D790 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 86.0 | °C | ASTM D648 |
| Additional Information |
|---|
| Tested at 23 ± 2°C (73.4 ± 3.6°F) and 50 ± 5% relative humidity unless otherwise noted |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 50 mm/min |
| 3 . | 500 mm/min |
| 4 . | 50 mm/min |
| 5 . | 500 mm/min |
| 6 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 141 HI HF | RTP Company | PP Copolymer | RTP |
| TOTAL Polypropylene PPR Z9421 | TOTAL Refining & Chemicals | PP Random Copolymer | TOTAL Polypropylene |
| ABSplus™ P430 | Stratasys | ABS | ABSplus™ |
| LONGLITE® PBT 4820-BK | CCP Group | PBT | LONGLITE® PBT |
| LNP™ THERMOCOMP™ MF008GS compound | SABIC Innovative Plastics | PP, Unspecified | LNP™ THERMOCOMP™ |