Menzolit® SMC 0290
| Category: | Polyester, TS , Thermoset Polyester |
| Manufacturer: | Menzolit Ltd (UK) |
| Trademark: | Menzolit® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | zafLPP_Menzolit-SMC-0290.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Menzolit® SMC 0290 is a sheet moulding compound based on unsaturated polyester resin. The product is glass fibre reinforced and contains mineral fillers. In case of fire the product doesn't melt, neither does it form droplets nor is smoke generation excessive. The material is compression moulded in heated steel moulds. It is recommended to work with chrome plated tools. The product contains no halogens. Menzolit® SMC 0290 is a specially formulated SMC processable by injection moulding. The gentle production process prevents the fiber from any damage. Parts made of SMC 0290 reach higher levels of strength and stiffness than BMC types. Thus, the material is favoured in those fields of application where BMC doesn't meet the demands regarding mechanical properties. SMC 0290 is serialized with a flammability of category V0 according to UL 94. Yellow Card is available for any tone! The glass content is on a level that combines good mouldability with good mechanical properties regarding strength and stiffness. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Part Marking Code (ISO 11469) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.70 | g/cm³ | ISO 1183 |
| Molding Shrinkage | |||
| -- 1 | 0.0 | % | DIN 53464 |
| -- | 0.10 | % | ISO 2577 |
| Water Absorption (Saturation, 23°C) | < 0.50 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (Compression Molded) | 12000 | MPa | ISO 527-2 |
| Tensile Stress (Yield, Compression Molded) | 60.0 | MPa | ISO 527-2 |
| Flexural Modulus (Compression Molded) | 10000 | MPa | ISO 178 |
| Flexural Stress (Compression Molded) | 143 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (Compression Molded) | 64 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | > 200 | °C | ISO 75-2/A |
| Continuous Use Temperature | 165 | °C | Internal Method |
| Glass Transition Temperature | 170 | °C | DSC |
| CLTE - Flow | 1.2E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+12 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | ohms·cm | IEC 60093 |
| Comparative Tracking Index | 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.00 mm) | V-0 | UL 94 | |
| Glow Wire Ignition Temperature | 960 | °C | IEC 60695-2-13 |
| Oxygen Index | 32 | % | ISO 4589-2 |
| Additional Information | Nominal Value | Test Method | |
|---|---|---|---|
| Glow Bar | Level BH 2 <= 10 | IEC 60707-3 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Mold Temperature | 135 to 150 | °C | |
| Injection Pressure | 8.00 to 10.0 | MPa |
| Note Message | |
|---|---|
| 1 . | Post Molding Shrinkage |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 800 GB 25 | RTP Company | Acetal (POM) Copolymer | RTP |
| Stanyl® TW250F6 | DSM Engineering Plastics | Nylon 46 | Stanyl® |
| NEFTEKHIM PE 5117P (18602) | Nizhnekamskneftekhim Inc. | LLDPE | NEFTEKHIM PE |
| Cheng Yu C1200 | Cheng Yu Plastic Company Limited | PC+ABS | Cheng Yu |
| PLEXIGLAS® Sheet Resist 65 | Evonik Industries AG | Acrylic (PMMA) | PLEXIGLAS® Sheet |