Witcom PEEK 3C-EM
| Category: | PEEK , Polyetheretherketone |
| Manufacturer: | Witcom Engineering Plastics B.V. |
| Trademark: | Witcom PEEK |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | zaTGwa_Witcom-PEEK-3C-EM.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Witcom PEEK 3C-EM is a Polyetheretherketone (PEEK) product filled with 15% carbon fiber. It is available in Europe. Characteristics include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.38 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow (3.00 mm) | 0.30 to 0.50 | % | ISO 2577 |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 0.45 | % | |
| Equilibrium, 23°C, 50% RH | 0.20 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | < 170 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 1.0 to 3.0 | % | ISO 527-2 |
| Flexural Modulus | 10000 | MPa | ISO 178 |
| Flexural Stress | 230 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | 9.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength | 40 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 315 | °C | ISO 75-2/A |
| CLTE - Flow | 2.3E-5 | cm/cm/°C | ISO 11359-2 |
| RTI Imp (3.00 mm) | 220 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+3 to 1.0E+5 | ohms | ASTM D257 |
| Volume Resistivity | 1.0E+4 to 1.0E+6 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.00 mm) | V-0 | ISO 1210 | |
| Glow Wire Flammability Index (1.60 mm) | 960 | °C | IEC 60695-2-12 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Badamid® LA70 GF50 HH | Bada AG | Nylon 66 | Badamid® |
| Hax™ HF 223F | Fainplast Compounds S.r.l | Polyolefin, Unspecified | Hax™ |
| HIDEN® M690 | YUHWA Korea Petrochemical Ind. Co., Ltd. | HDPE | HIDEN® |
| Hostalen GM 5010 T3 black | LyondellBasell Industries | HDPE | Hostalen |
| LNP™ THERMOCOMP™ LC008EXQ compound | SABIC Innovative Plastics | PEEK | LNP™ THERMOCOMP™ |