A high rate, midrange gloss, PVC powder, extrusion compound for exterior/interior applications. Typical test results for ASTM D-4216. This is a Rigid PVC formulation per the requirements of AAMA 303-05. Testing was performed on actual window parts with a wall thickness of 0.100". This material meets/exceeds cell class 1-20131-13** as required in ASTM D-4726. Testing was performed by Dallas Laboratory, Inc., July 2006. |
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.44 to 1.48 | g/cm³ | ASTM D792 |
| PVC Cell Classification | 1-41343-12 | ASTM D4216 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness 1(Shore D, 22°C) | 75 to 81 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (22°C) | 2630 | MPa | ASTM D638 |
| Tensile Strength (Yield, 22°C) | 45.1 | MPa | ASTM D638 |
| Flexural Modulus (22°C) | 2650 | MPa | ASTM D790 |
| Flexural Strength (22°C) | 80.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (22°C) | 690 | J/m | ASTM D256 |
| Drop Impact Resistance | ASTM D4226 | ||
| 22°C, Extruded at 370 to 380° F melt temperature 2 | 57.8 | J/cm | |
| 22°C, Extruded at 370 to 380° F melt temperature 3 | > 125 | J/cm |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 69.4 | °C | ASTM D648 |
| CLTE - Flow (22°C) | 4.5E-5 | cm/cm/°C | ASTM D696 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Burning Rate | ASTM D635 | ||
| AEB | < 5.00 | ||
| ATB | < 5.00 |
| Note Message | |
|---|---|
| 1 . | Instantaneous |
| 2 . | Procedure A |
| 3 . | Procedure B |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shandong Aobang TPU-Polyether 85-A | Shandong Aobang Chemical Technology Co.,Ltd. | TPU-Polyether | Shandong Aobang TPU-Polyether |
| Unichem 6511-02 | Colorite Polymers | PVC, Unspecified | Unichem |
| Fainplast PVC CKL 0222 | Fainplast Compounds S.r.l | PVC, Unspecified | Fainplast PVC |
| Lutene® XL8080NTS | LG Chem Ltd. | PE, Unspecified | Lutene® |
| TARFLON™ RE1900 | Idemitsu Kosan Co., Ltd. | PC | TARFLON™ |