TROGAMID® Care MX73
| Category: | Nylon, Unspecified , Polyamide |
| Manufacturer: | Evonik Industries AG |
| Trademark: | TROGAMID® Care |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | zZ5WWW_TROGAMID-Care-MX73.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
Microcrystalline TROGAMID® Care MX is the material of choice for all applications dealing with pharmaceutical formulations, lipids or aggressive disinfectants, since it exhibits an exceptional resistance towards chemicals and stress-cracking. Examples include fluid and drug delivery equipment such as stop-cocks, dialyzer parts, housings, covers or hearing aids. Target areas of application for TROGAMID® Care MX compounds include fluid and drug delivery systems, surgical instruments, housings, monitoring and imaging devices and durable medical equipment. All advantages at a glance
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.02 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow : 2.00 mm | 0.80 | % | |
| Flow : 2.00 mm | 0.65 | % | |
| Water Absorption (Saturation, 23°C) | 3.5 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 81 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1400 | MPa | ISO 527-2 |
| Tensile Stress (Yield, 23°C) | 60.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Yield, 23°C) | 8.0 | % | ISO 527-2/50 |
| Nominal Tensile Strain at Break (23°C) | > 50 | % | ISO 527-2/50 |
| Flexural Modulus | 1700 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C, Complete Break | 11 | kJ/m² | |
| 23°C, Complete Break | 14 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | No Break | ||
| 23°C | No Break |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 122 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 108 | °C | ISO 75-2/A |
| Glass Transition Temperature 1 | 140 | °C | ISO 11357-2 |
| Vicat Softening Temperature | |||
| -- | 137 | °C | ISO 306/A |
| -- | 130 | °C | ISO 306/B |
| Melting Temperature (DSC) 2 | 250 | °C | ISO 11357 |
| CLTE | ISO 11359-2 | ||
| Flow : 23 to 55°C | 9.0E-5 | cm/cm/°C | |
| Transverse : 23 to 55°C | 9.0E-5 | cm/cm/°C |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.800 mm | HB | ||
| 1.60 mm | HB |
| Note Message | |
|---|---|
| 1 . | 10 K / min |
| 2 . | 2nd Heating |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| VITAMIDE® BX10BK6660 | Jackdaw Polymers | Nylon 6 | VITAMIDE® |
| Trilliant™ HC X THC 1101 Natural | PolyOne Corporation | Copolyester | Trilliant™ HC |
| Karina IVORY PVC COMPOUND -E 832-35/ 1-Y-ERA-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Plaslube® J-1305/30/TF/15 | Techmer Engineered Solutions | PPS | Plaslube® |
| Plaslube® PA6 GF40 ML2 HS UV BK | Techmer Engineered Solutions | Nylon 6 | Plaslube® |