Michirene S13100
| Category: | PS (HIPS) , High Impact Polystyrene |
| Manufacturer: | API Polymers, Inc. |
| Trademark: | Michirene |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | zYo0Ss_Michirene-S13100.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Michirene S13100 is a high impact polystyrene product,. It is available in North America. The main characteristics are: impact resistance. |
| General Information | |
|---|---|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.04 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | 8.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.60 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1590 | MPa | ASTM D638 |
| Tensile Strength (Yield) | 26.9 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 45 | % | ASTM D638 |
| Flexural Modulus - Tangent | 1930 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 110 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 81.0 | °C | ASTM D648 |
| Additional Information |
|---|
| Drying is usually not necessary |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 77.0 | °C | |
| Drying Time | 2.0 | hr | |
| Rear Temperature | 204 | °C | |
| Middle Temperature | 210 | °C | |
| Front Temperature | 216 | °C | |
| Nozzle Temperature | 221 | °C | |
| Processing (Melt) Temp | 227 | °C | |
| Mold Temperature | 49.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 3399 X 136178 A | RTP Company | PVDF | RTP |
| Nanjing Hongrui PA66 A1000 | Nanjing Hongrui Engineering Plastics Co., Ltd. | Nylon 66 | Nanjing Hongrui PA66 |
| GAPEX® HP RPP40EB86HB | Ferro Corporation | PP Homopolymer | GAPEX® HP |
| LG ABS HF380 | LG Chem Ltd. | ABS | LG ABS |
| OmniLon™ PA6/6 GR33 HSh | OMNI Plastics, LLC | Nylon 66 | OmniLon™ |