SCLAIR® 99K
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | NOVA Chemicals |
| Trademark: | SCLAIR® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | zXve7o_SCLAIR-99K.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SCLAIR®99K is a high density polyethylene material,. This product is available in North America,. SCLAIR®The main features of 99K are:
Typical application areas include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.961 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.72 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 69 | ASTM D2240 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 38 | µm | |
| secant modulus | ASTM D882 | ||
| 1% secant, MD : 38 µm, blown film | 830 | MPa | ASTM D882 |
| 1% secant, TD : 38 µm, blown film | 1330 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 38 µm, blown film | 27.0 | MPa | ASTM D882 |
| TD : Yield, 38 µm, blown film | 22.0 | MPa | ASTM D882 |
| MD : Broken, 38 µm, blown film | 39.0 | MPa | ASTM D882 |
| TD : Broken, 38 µm, blown film | 22.0 | MPa | ASTM D882 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 128 | °C | ASTM D1525 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 38.0 µm, Blown Film) | 5 | ASTM D2457 | |
| Haze (38.0 µm, Blown Film) | 78 | % | ASTM D1003 |
| Extrusion instructions |
|---|
| Blow-up Ratio: 2.5:1 to 4:1 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 283 D TFE 10 SI 2 | RTP Company | Nylon 6/12 | RTP |
| SPI CPPFG18CNAT | Service Polymers, Inc. | PP Impact Copolymer | SPI |
| TABOREN PH 89 T 20 | SILON s.ro | PP Homopolymer | TABOREN |
| BUP 624 | Bonyan Kala Chemie Company | Polyester, TS | BUP |
| Hostalen ACP 5331 A | LyondellBasell Industries | HDPE | Hostalen |